Rasool, Ghulam and Stack, Margaret (2014) Mapping the role of Cr content in dry sliding of steels : comparison between maps for material
نویسندگان
چکیده
In this work, a study of the wear transition regimes was carried out for a pin-on-disk sliding couple, involving two steels of different hardness and Cr contents. Dry sliding wear behaviour of the more highly alloyed stainless steel was dominated by adhesive wear and tribo-oxidation at relatively low sliding speeds and by mixed and adhesive wear at high speeds and loads. In contrast, oxidative wear was more predominant for the lower alloyed steel. The individual wear maps generated for the individual components i.e. material and counterface are discussed in the context of the wear mechanisms observed in the tribological contact.
منابع مشابه
Comparison of different algorithms for land use mapping in dry climate using satellite images: a case study of the Central regions of Iran
The objective of this research was to determine the best model and compare performances in terms of producing landuse maps from six supervised classification algorithms. As a result, different algorithms such as the minimum distance ofmean (MDM), Mahalanobis distance (MD), maximum likelihood (ML), artificial neural network (ANN), spectral anglemapper (SAM), and support vector machine (SVM) were...
متن کاملDetermining the Hot Deformation Temperature Range of Medium Carbon Ni-Cr-Mo Low Alloy Steels using Hot Tensile and Hot Torsion Tests
The aim of this study was to investigate the suitable temperature range for hot deformation of three medium carbon Ni-Cr-Mo low alloy steels by hot tensile and hot torsion tests. Hot tensile tests were carried out in the te,prature range of 850-1150°C at a constant strain rate of 0.1 s-1 until fracture. Then, the tensile flow behavior, hot ductility and microstructural evolution of the steels w...
متن کاملPHASE STABILITY AND SEMICONDUCTING BEHAVIOUR OF LOW ACTIVATION AUSTENITIC MN-CR STEELS
Four compositions of austenitic Mn-Cr steels have been developed successfully for in-vessel component materials in power plant industry. The phase stability of these Mn-Cr steels was studied by and X-ray diffraction (XRD) patterns. XRD patterns have shown that the matrix of these Mn-Cr steels is a single γ-phase structure. The potentiodynamic polarisation curves suggested that these fabricated ...
متن کاملEvaluation of corrosion behaviour on Mn-Cr austenitic steels using 0.1 M HCl solution
One of the attractive low activation steels is the austenitic Mn-Cr steel from the view point of waste disposal because of few long-lived nuclides. In this paper, three types of Mn-Cr austenitic steels were fabricated by vacuum induction furnace. Then plates with 10 mm thickness were fabricated by hot-rolling. The physical metallurgy of these steels was studied by the corrected Schaeffler diagr...
متن کاملInfluence of High Strain Rates on the Mechanical Behavior of High-Manganese Steels
In this work, dynamic mechanical properties of three high-manganese steels with TRIP/TWIP or fully TWIP characteristics are studied. High strain rate experiments in the range of true strain rates between ~500 and 1800 /s are conducted using a dynamic torsional testing setup. All the three steels show a positive strain rate sensitivity in the intermediate range of strain rates (up to 500 /s). Bu...
متن کامل