Surface modification of Ti-4Al-2V alloy by nitrogen implantation
نویسندگان
چکیده
Ti-4Al-2V is a new type of alpha titanium alloy that suitable for the application in high-temperature and high-pressure water/steam environment. Ti-4Al-2V can be used in marine engineering, nuclear power industry. In this paper the surface characterization of the Ti-4Al-2V implanted with 75 keV nitrogen with fluences of 3 × 1017 and 8 × 1017 N+/cm2 is investigated by glancing-incidence XRD, XPS and microhardness. The results show that new phase TiN are formed after N implantation in the surface region. The nitrogen implantation increases the surface hardness up to 340 and 260% for fluence of 8 × 1017 and 3 × 1017 N+/cm2, respectively. The enhancement of hardness is related to the formation of TiN and irradiation induced hardness. C © 2006 Springer Science + Business Media, Inc.
منابع مشابه
TIG Surface Alloying of Ti-6Al-4V with Nitrogen and Chromium for Improved Tribological Properties
Due to special properties such as low density, high strength and high corrosion resistance Ti-6Al-4V alloy has been used extensively in various industries, especially in the aerospace aspects. However the major problem of this alloy is its poor tribological properties under relatively high loads. In the present study, in order to improve the tribological properties of mentioned alloy, chromium ...
متن کاملOptimization of Material Removal Rate and Surface Roughness for WEDM of Titanium Alloy (Ti-4.5Al-2V) Using Taguchi Method
In this paper, wire electric discharge machining (WEDM) of Titanium alloy (Ti-4.5Al-2V) is studied. In WEDM, the prime objective in cutting operation is to achieve the highest possible cutting speed along with desirable surface finish without sacrificing productivity. It is evident that a high material removal rate and a very good surface finish can never be achieved simultaneously in WEDM. Sel...
متن کاملDesign of a nitrogen-implanted titanium-based superelastic alloy with optimized properties for biomedical applications.
In this study, a superelastic Ni-free Ti-based biomedical alloy was treated in surface by the implantation of nitrogen ions for the first time. The N-implanted surface was characterized by X-ray diffraction, X-ray photoelectron spectroscopy, and secondary ion mass spectroscopy, and the superficial mechanical properties were evaluated by nano-indentation and by ball-on-disk tribological tests. T...
متن کاملEffect of Gas-Diffusion Oxynitriding on Microstructure and Hardness of Ti-6Al-4V Alloys
The commercially available titanium alloy, Ti-6Al-4V, was oxynitrided in the deoxygenated nitrogen gas at high temperatures followed by cooling in oxygen-containing nitrogen in order to analyze the influence of oxynitriding parameters on the phase modification, hardness, and the microstructural evolution of the oxynitrided coating. The surface microhardness of the oxynitrided alloy increased du...
متن کاملIon-Doped Silicate Bioceramic Coating of Ti-Based Implant
Titanium and its alloy are known as important load-bearing biomaterials. The major drawbacks of these metals are fibrous formation and low corrosion rate after implantation. The surface modification of biomedical implants through various methods such as plasma spray improves their osseointegration and clinical lifetime. Different materials have been already used as coatings on biomedical implan...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2006