Abstract: Dipyridamole Enhances Osteogenesis of 3D-Printed Bioactive Ceramic Scaffolds in Calvarial Defects
نویسندگان
چکیده
METHODS: Custom 3DPBC scaffolds designed to present lattice-based porosity only towards the dural surface were either coated with collagen (control) or coated with collagen and immersed in a 100 μM concentration dipyridamole (DIPY) solution. Sheep (n=5) were subjected to 2 ipsilateral trephine-induced (11 mm diameter) calvarial defects. Either a control or a DIPY scaffold was placed in each defect and the surgery was repeated on the contralateral side 3 weeks later. Following sacrifice, defects were evaluated through microcomputed tomography and histologic analysis for bone, scaffold, and soft tissue quantification throughout the defect. Parametric and non-parametric methods were utilized to determine statistical significance based on data distribution.
منابع مشابه
Abstract 47. Dipyridamole-Containing 3D-Printed Bioactive Ceramic Scaffolds for the Treatment of Calvarial Defects: An Experimental Study in Sheep
T ueday, M arch 8, 2017 METHODS: One hundred fifty-eight patients with 277 expanded skin cases during 2010 to 2014 were reviewed and photograph-evaluated for the expanded skin texture and regenerative condition. Overall texture of the expanded skin flaps (Good, Fair, Poor) were evaluated and documented by senior attending surgeons. The occurrence of five indications of skin regeneration limitat...
متن کاملAbstract: Dipyridamole Releasing 3D Printed Bioactive Ceramic Scaffolds with Osseoconductive Geometries Promote Craniofacial Bone Regeneration
METHODS: Custom 3DPBC scaffolds designed to present lattice-based porosity only towards the dural surface were either coated with collagen (control) or coated with collagen and immersed in a 100 μM concentration dipyridamole (DIPY) solution. Sheep (n=5) were subjected to 2 ipsilateral trephine-induced (11 mm diameter) calvarial defects. Either a control or a DIPY scaffold was placed in each def...
متن کاملThree dimensional printing of calcium sulfate and mesoporous bioactive glass scaffolds for improving bone regeneration in vitro and in vivo
In the clinic, bone defects resulting from infections, trauma, surgical resection and genetic malformations remain a significant challenge. In the field of bone tissue engineering, three-dimensional (3D) scaffolds are promising for the treatment of bone defects. In this study, calcium sulfate hydrate (CSH)/mesoporous bioactive glass (MBG) scaffolds were successfully fabricated using a 3D printi...
متن کاملNano-biphasic calcium phosphate/polyvinyl alcohol composites with enhanced bioactivity for bone repair via low-temperature three-dimensional printing and loading with platelet-rich fibrin
Background and aim As a newly emerging three-dimensional (3D) printing technology, low-temperature robocasting can be used to fabricate geometrically complex ceramic scaffolds at low temperatures. Here, we aimed to fabricate 3D printed ceramic scaffolds composed of nano-biphasic calcium phosphate (BCP), polyvinyl alcohol (PVA), and platelet-rich fibrin (PRF) at a low temperature without the add...
متن کاملSystematical Evaluation of Mechanically Strong 3D Printed Diluted magnesium Doping Wollastonite Scaffolds on Osteogenic Capacity in Rabbit Calvarial Defects
Wollastonite (CaSiO3; CSi) ceramic is a promising bioactive material for bone defect repair due to slightly fast degradation of its porous constructs in vivo. In our previous strategy some key features of CSi ceramic have been significantly improved by dilute magnesium doping for regulating mechanical properties and biodegradation. Here we demonstrate that 6 ~ 14% of Ca substituted by Mg in CSi...