The effect of fiber insertion on fracture resistance of endodontically treated molars with MOD cavity and reattached fractured lingual cusps.
نویسندگان
چکیده
In this study, the effect of flowable composite reinforced with a leno wave ultra high modulus (LWUHM) polyethylene fiber (Ribbond) on fracture resistance of endodontically treated molars with MOD cavity and lingual cuspal fracture was evaluated. Sixty sound extracted human mandibular molars were randomly assigned to six groups (n = 10). Group 1 served as control. Teeth in groups 2-6 received root canal treatment and a MOD cavity preparation. Teeth in group 2 were kept unrestored. Lingual walls of specimens in groups 3-6 were fractured at the CEJ and reattached (C&B Super-Bond). Group 3 was kept unrestored, and group 4 was restored with a composite resin (CR) (AP-X). In group 5, a flowable resin (FR, Protect Liner F) and in group 6, a Ribbond in combination with FR were inserted inside the cavity before CR restoration. After finishing and polishing, the specimens were subjected to compressive loading perpendicular to the occlusal surface at a crosshead speed of 1 mm/min. The mean load necessary to fracture were recorded in Newton and the results were statistically analyzed. MOD cavity preparation reduced fracture resistance of endodontically treated teeth (p < 0.05). Fracture resistance of rebonded fractured specimens was found to be similar to that of the nonfractured samples (p > 0.05). Use of LWUHM polyethylene fiber Ribbond increased fracture strength of endodontically treated molar teeth with MOD cavity preparation and cuspal fracture (p < 0.05). As a result, it was concluded that the insertion of Ribbond inside the cavity has a positive effect on fracture strength of endodontically treated molar teeth with MOD cavity preparation and cuspal fracture.
منابع مشابه
In Vitro Evaluation of the Effect of Tooth Structure Loss on Fracture Resistance of Endodontically Treated Teeth
Introduction: Since preserving the structure of treated teeth is a critical success factor, studying the effects of tooth structure loss on fracture resistance of the tooth tissue appears necessary. The aim of this study was to evaluate the consequences of the loss of different tissues regarding fracture resistance of teeth undergoing root canal treatment without the use of indirect restoration...
متن کاملStress Distribution in Four Restorative Methods in Endodontically Treated Maxillary Premolar: A 3D Finite Element Analysis
Introduction: the Restoration of endodontically treated teeth is critical, and the Awareness of stresses developed by oblique and vertical forces in restorative methods take a great role in treatment plans. Due to the anatomical shape and inherent form of the stress distribution premolars, could be lost by fractures. Some fractures such as vertical fracture which is probable in...
متن کاملمقایسه آزمایشگاهی اثر ریلاین فایبرپست با دو نوع کامپوزیت قابل سیلان بر مقاومت به شکست دندان های سانترال ماگزیلاری درمان ریشه شده
Background and Objective: Relining fiber posts with flowable composites is a procedure used for strengthening the weak walls of endodontically treated teeth. The aim of this study was to evaluate the effect of relining fiber posts with two types of flowable composites on the fracture resistance of the endodontically treated teeth. Materials and Methods: In this laboratory experimental study, 3...
متن کاملEffect of different onlay systems on fracture resistance and failure pattern of endodontically treated mandibular molars restored with and without glass fiber posts.
PURPOSE To investigate the relationship between post and core build-up materials on the fracture resistance of endodontically treated teeth restored with different onlay restorations. METHODS 60 mandibular molars were endodontically treated and divided into three experimental groups that received one of the following onlay restorations: gold onlays, glass ceramic onlays (Empress I), or resin ...
متن کاملIn Vitro Effect of Zirconia and Zirconia Enriched Glass Fiber Composite Posts on Fracture Resistance of Endodontically Treated Teeth
Objective: Despite the advantages of esthetic posts, lack of studies on their fracture resistance has limited their clinical use. This study aimed to compare the effect of two types of esthetic posts namely zirconia and zirconia enriched glass fiber composite posts on fracture resistance of endodontically treated teeth against compressive forces. Methods: This in vitro study was conducted o...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Journal of biomedical materials research. Part B, Applied biomaterials
دوره 79 1 شماره
صفحات -
تاریخ انتشار 2006