Experimental and Computational Study of Ductile Fracture in Small Punch Tests
نویسندگان
چکیده
A unified experimental-computational study on ductile fracture initiation and propagation during small punch testing is presented. Tests are carried out at room temperature with unnotched disks of different thicknesses where large-scale yielding prevails. In thinner specimens, the fracture occurs with severe necking under membrane tension, whereas for thicker ones a through thickness shearing mode prevails changing the crack orientation relative to the loading direction. Computational studies involve finite element simulations using a shear modified Gurson-Tvergaard-Needleman porous plasticity model with an integral-type nonlocal formulation. The predicted punch load-displacement curves and deformed profiles are in good agreement with the experimental results.
منابع مشابه
Prediction of forming limit curves (FLD, MSFLD and FLSD) and necking time for SS304L sheet using finite element method and ductile fracture criteria
Forming limit curves are used as a parameter in finite element analysis to control the material's level of formability. In this research, forming limit diagram (FLD) of SS304L sheet was obtained by ABAQUSfinite element software. In practice, the experimental determination of a forming limit curve is a very time-consuming procedure which requires special and expensive equipment. Forming limit di...
متن کاملDuctile Damage Evolution under Triaxial Stress Conditions: Computational and Experimental Evaluations
The continuum mechanic simulation of micro-structural damage process is important in the study of ductile fracture mechanics. In this paper, the continuum damage mechanics model formulation proposed by Lematire has been validated against ductile damage evolution experimentally measured in A533B-C1 steel under stress triaxiality conditions. First, a 
procedure to identify the model parameters...
متن کاملDuctile Damage Evolution under Triaxial Stress Conditions: Computational and Experimental Evaluations
The continuum mechanic simulation of micro-structural damage process is important in the study of ductile fracture mechanics. In this paper, the continuum damage mechanics model formulation proposed by Lematire has been validated against ductile damage evolution experimentally measured in A533B-C1 steel under stress triaxiality conditions. First, a procedure to identify the model parameters f...
متن کاملEvaluation of Ductile Damage Criteria in Hot Forming Processes
The process of ductile fracture which occurs due to the accumulation, growth and combination of defects or cracks of material is called ductile damage. Failure in materials can be predicted, using damage mechanics and damage criteria. On the other hand, most of the materials depended to the manufacturing process, are formed in warm or hot conditions so that; the temperature also affects on the ...
متن کاملSmall punch tensile/fracture test data and 3D specimen surface data on Grade 91 ferritic/martensitic steel from cryogenic to room temperature
Raw data from small punch tensile/fracture tests at two displacement rates in the temperature range from -196 °C to room temperature on Grade 91 ferritic/martensitic steel are presented. A number of specimens were analyzed after testing by means of X-ray computed tomography (CT). Based on the CT volume data detailed 3D surface maps of the specimens were established. All data are open access and...
متن کامل