High-pressure crystallization of isotactic polypropylene droplets
نویسندگان
چکیده
Dispersions of isotactic polypropylene (PP) particles in polystyrene (PS) were produced by interfacially driven breakup of nanolayers in multilayered systems that were fabricated by means of layer-multiplying coextrusion. The droplet size was controlled by the individual PP layer thickness ranging from 12 to 200 nm. In addition, PP was melt blended with PS to produce PP droplets larger than those formed by breakup of nanolayers. The dispersions of PP particles in the PS matrix were melted and annealed under high pressure of 200 MPa. Only the largest PP droplets, with average sizes of 170 μm, crystallized predominantly in the γ form. In the 42-μm droplets obtained by breakup of 200 nm layers, a minor content of the γ form was found whereas the smaller droplets obtained by breakup of the thinner nanolayers contained the α form and/or the mesophase. The results showed that the γ phase formed only in the droplets sufficiently large to contain the most active heterogeneities nucleating PP crystallization under atmospheric pressure. It is concluded that the presence of nucleating heterogeneities is necessary for crystallization of PP in the γ form under high pressure.
منابع مشابه
The role of nucleating agents in high-pressure-induced gamma crystallization in isotactic polypropylene
Nucleation of the γ-form in isotactic polypropylene (PP) under high pressure was investigated. Three nucleating agents were used to nucleate crystallization of PP under atmospheric pressure: commercial Hyperform HPN-20E from Milliken Chemical, poly(tetrafluoroethylene) particles nucleating the α-form, and calcium pimelate nucleating the β-form. Crystallization of neat PP and PP with addition of...
متن کاملControlled Crystallization of Isotactic Polypropylene Based on ┙/┚ Compounded Nucleating Agents: From Theory to Practice
متن کامل
Crystal structure of the trigonal form of isotactic polypropylene as an example of density-driven polymer structure.
Propene-hexene copolymers crystallize in a new polymorphic form of isotactic polypropylene when the concentration of hexene is higher than nearly 10-15 mol %. The hexene units are included in the crystals, inducing an increase of density that allows crystallization of 3-fold helical chains in a trigonal unit cell according to the space group R3c or Rc, where the helical symmetry of the chains i...
متن کاملInfluence of the temperature on flow-induced crystallization of isotactic polypropylene and propylene-ethylene random copolymer
BOITOUT, Hugo, "Influence of the temperature on flow-induced crystallization of isotactic polypropylene and propylene-ethylene random copolymer" (2014). Influence of the temperature on flow-induced crystallization of isotactic polypropylene and propylene-ethylene random copolymer Influence of the temperature on flow-induced crystallization of isotactic polypropylene and propylene-ethylene rando...
متن کاملEffect of Sorbitol Templates on the Preferential Crystallographic Growth of Isotactic Polypropylene Wax
The crystallization of isotactic polypropylene wax (iPP) in the presence of different sorbitol structures was studied. Dibenzylidene Sorbitol (DBS), as well as two of its derivatives with one or two methyl groups in the DBS molecule (MDBS and DMDBS, respectively), were tested as nanometer-size fibrillar templates. The early nucleation stage and crystal morphology were analyzed in Real-Time Wide...