Fatigue growth of multiple-cracks near a row of fastener-holes in a fuselage lap-joint
نویسندگان
چکیده
The fatigue growth of multiple cracks, of arbitrary lengths, emanating from a row of fastener holes in a bonded, riveted, lap joint in a pressurized aircraft fuselage is studied. The effects of residual stresses due to a rivet misfit, and of plastic deformation near the hole, are included. A Schwartz Neumann alternating method which uses the analytical solution for a row of multiple colinear cracks in an infinite sheet (the crack-faces being subject to arbitrary tractions), is developed to analyze this MSD problem on a personal computer. It is found that for a range of crack lengths, a phenomena wherein the shorter cracks may grow faster than longer cracks may exist.
منابع مشابه
Growth of Multiple Cracks and Their Linkup in a Fuselage Lap Joint
An issue of concern in aging aircraft is the growth of multiple cracks emanating from a row of fastener holes, typically in a pressurized aircraft fuselage lap splice. This multisite damage (MSB), or widespread fatigue damage, if allowed to progress, can suddenly become catastrophic. The understanding of the failure behavior dictates the level of compromise between safety and economy. The compl...
متن کاملFracture and fatigue analysis of curved or kinked cracks near fastener holes
The finite element alternating method is an attractive and efficient method for calculating the stress intensity factor of cracks emanating from fastener holes such as the problem of multiple site damage (MSD) at the fuselage skin of aging aircraft. While the alternating method has been used to solve various engineering problems in assessing the structural integrity of aging aircraft, this meth...
متن کاملMixed mode fatigue growth of curved cracks emanating from fastener holes in aircraft lap joints
The ®nite element alternating method is extended further for analyzing multiple arbitrarily curved cracks in an isotropic plate under plane stress loading. The required analytical solution for an arbitrarily curved crack in an in®nite isotropic plate is obtained by solving the integral equations formulated by Cheung and Chen (1987a, b). With the proposed method several example problems are solv...
متن کاملResidual Strength Analyses of Riveted Lap-Splice Joints
Aging aircraft may develop multiple-site damage (MSD) that can reduce the structural integrity of fuselage structures. The existence of small cracks emanating from adjacent rivet holes in a fuselage lap-splice joint is of major concern. Small collinear cracks greatly reduce the residual strength of a panel with a lead crack. Recent studies predicting the residual strength of flat and curvilinea...
متن کاملExperimental Investigation and Numerical Prediction of Fatigue Life in Force Fitted Fastener Holes
In this paper, the effect of interference fit on fatigue life of holed plate of mechanical joints was investigated experimentally. Fatigue tests were carried out on the holed specimens of Al-alloy 7075-T6 alloy. The interference fit process consists of force fitting a fastener into the hole with a negative clearance (diameter of the fastener is larger than of the hole) that produces beneficial ...