Liquid Foam Templates Associated with the Sol-Gel Process for Production of Zirconia Ceramic Foams

نویسندگان

  • Cristiane Carolina Beozzo
  • Marinalva Aparecida Alves-Rosa
  • Sandra Helena Pulcinelli
  • Celso Valentim Santilli
چکیده

The unique properties of ceramic foams enable their use in a variety of applications. This work investigated the effects of different parameters on the production of zirconia ceramic foam using the sol-gel process associated with liquid foam templates. Evaluation was made of the influence of the thermal treatment temperature on the porous and crystalline characteristics of foams manufactured using different amounts of sodium dodecylsulfate (SDS) surfactant. A maximum pore volume, with high porosity (94%) and a bimodal pore size distribution, was observed for the ceramic foam produced with 10% SDS. Macropores, with an average size of around 30 μm, were obtained irrespective of the SDS amount, while the average size of the supermesopores increased systematically as the SDS amount was increased up to 10%, after which it decreased. X-ray diffraction analyses showed that the sample treated at 500 °C was amorphous, while crystallization into a tetragonal metastable phase occurred at 600 °C due to the presence of sulfate groups in the zirconia structure. At 800 and 1000 °C the monoclinic phase was observed, which is thermodynamically stable at these temperatures.

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

A New Step-based Photoreactor for Degradation of Acid Dye using N-TiO2-P25-coated Ceramic Foam under Visible Light

In the present study, a new step-based photoreactor was presented to investigate the degradation of Acid Red 73 under visible light irradiation. Four N-TiO2-coated alumina foams prepared by the modified sol-gel process were arranged in each step as photocatalyst. The experimental design methodology was employed to assess the interaction between the operational parameters in the step-...

متن کامل

The production of Ceramic Thin Films by Sol-Gel Method

The purpose of this work was to production of ceramic thin films by using of Sol-Gel process. For this purpose deposition of SiO2 on substrates of soda-lime glasses has been carried out. Coating treatments on prepared specimen were conducted in a Sol solution by means of dipping at various times. After drying and performing appropriate heat treatment on each sample, the thickness of coated laye...

متن کامل

The production of Ceramic Thin Films by Sol-Gel Method

The purpose of this work was to production of ceramic thin films by using of Sol-Gel process. For this purpose deposition of SiO2 on substrates of soda-lime glasses has been carried out. Coating treatments on prepared specimen were conducted in a Sol solution by means of dipping at various times. After drying and performing appropriate heat treatment on each sample, the thickness of coated laye...

متن کامل

Pore surface fractal dimension of sol-gel derived nanoporous SiO2-ZrO2 membrane

In this work, SiO2 –ZrO2 mixed oxides was prepared by the polymeric sol–gel route. The characterization of pore structure, which determines the permeation process of membrane, is of great importance. So far, most investigations have focused on such pore structure as specific surface area and pore size distribution, but the surface fractal, the important parameter reflecting the roughness of por...

متن کامل

Application of the Properties of Nano-Silica Gel Coatings: Modification of the Styrofoam Cup

The temperatures of standard glassware and ceramics are nearly impossible to tell just by sight. Therefore, burns from touching heated surfaces are common in the laboratory and in the kitchen. The sol-gel process is a safe method to create foam under ambient conditions. Adding different chemical compounds causes the foam to have varying physical and chemical characteristics. This project focuse...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

عنوان ژورنال:

دوره 6  شماره 

صفحات  -

تاریخ انتشار 2013