Sealing ability of mineral trioxide aggregate, calcium phosphate cement, and glass ionomer cement in the repair of furcation perforations.

نویسندگان

  • Prabath Singh
  • Joseph Paul
  • Abdul Aziz Al-Khuraif
  • Sajith Vellappally
  • Hassan Suliman Halawany
  • Mohamed Hashim
  • Nimmi Biju Abraham
  • Vimal Jacob
  • Rooban Thavarajah
چکیده

OBJECTIVES The purpose of this study was to evaluate the in vitro sealing ability of three repair materials. Mineral trioxide aggregate (MTA; Group A), calcium phosphate cement (CPC; Group B), and light cured glass ionomer cement (GIC; Group C) when used to repair the perforation created in the pulpal floor of fifty extracted human permanent molars. MATERIALS AND METHODS Preparation of access openings and furcation perforations were done, and the teeth divided into five experimental groups (A, B, C) including two controls (D, E) with ten samples in each group randomly. Following the repair procedure, the pulp chambers and access openings were filled with composite resin and immersed in 2% methylene blue solution for 48 hours. The teeth were sectioned longitudinally and the linear dye penetration measured under a stereomicroscope. RESULTS The comparison of the linear length of micro-leakage (mm) among the experimental groups revealed no significant difference (p = 0.332). On calculating the percentage of depth of leakage to the total length of the perforation, it was observed that the mean leakage was 35.5% in Group A, 53.6% in Group B and the highest, 87.5% in Group C. The mean of leakage percentage was statistically significant by Kruskal-Wallis test (p = 0.003). The results indicated that the dye penetration used as furcation perforation repair material was least with mineral trioxide aggregate. Comparing the depth of penetration of dye, 50% of the Group A samples showed less than 25% of depth penetration. While 40% of Group B cases had more than 50% dye penetration. In our study, all Group C teeth had > or = 50% dye penetration. CONCLUSIONS The present study indicated that GIC had the greatest dye penetration followed by CPC and MTA. Mineral trioxide aggregate and calcium phosphate cement had comparatively better sealing ability than glass ionomer cement.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

In vitro evaluation of bacterial leakage through different perforation repair materials of teeth.

PURPOSE This study was conducted to evaluate micro-leakage through different furcation repair dental materials which are used to repair iatrogenic perforations in teeth. Six commercially available dental materials high copper amalgam, glass ionomer cements (GIC) Fuji II and Fuji IX, intermediate restorative material (IRM), mineral trioxide aggregate (MTA) and fully injectable calcium phosphate ...

متن کامل

Sealing ability of mineral trioxide aggregate and Portland cement for furcal perforation repair: a protein leakage study.

The purpose of this study was to compare the sealing ability of gray mineral trioxide aggregate (GMTA), white MTA (WMTA), and both white and gray Portland cement as furcation perforation repair materials. A total of 120 human mandibular first molars were used. After root canal obturation and preparation of furcal perforations the specimens were randomly divided into four groups of 25 teeth each...

متن کامل

An In-Vitro Comparative Evaluation Of Sealing Ability Of Resin Modified Glass Ionomer Cement, Mineral Trioxide Aggregate And BiodentineAs A Furcation Repair Material: Analysis By Confocal Laser Microscopy

1 Professor, Director Principal and H.O.D, Department of Conservative Dentistry & Endodontics Surendera Dental College and Research Institute, Sri Ganganagar. INDIA 2 Post graduate student, Department of Conservative Dentistry & Endodontics Surendera Dental College and Research Institute, Sri Ganganagar. INDIA 3 Professor, Department of Conservative Dentistry & Endodontics Surendera Dental Coll...

متن کامل

Repair of Furcal Perforation with Mineral Trioxide Aggregate: Case Report

Furcal perforation is usually an undesired complication that can occur during preparation of an endodontic access cavities or exploring canal orifice of multirooted teeth. Inadequacy of the repair materials has been a contributing factor to the poor outcome of repair procedures. On the basis of the recent physical and biologic property studies of the relatively new introduced mineral trioxide a...

متن کامل

Evaluation of Microleakage of Bioactive Glass, Bioactive Glass-Hydroxyapatite and Mineral Trioxide Aggregate-An in Vitro Study

Introduction: The aim of this study was to evaluate the sealing ability of Bioactive glass (BG) and Bioactive glass-Hydroxyapatite (BG-HA) in comparison to Mineral Trioxide Aggregate (MTA). Methods: The sealing ability of Bioactive glass and Bioactive glass-hydroxyapatite mixed with glass ionomer cement and Mineral Trioxide Aggregate used as retrograde filling material was assessed by bacterial...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Acta medica

دوره 56 3  شماره 

صفحات  -

تاریخ انتشار 2013