Elastic behaviour of Sn doped Ni-Zn ferrites
نویسندگان
چکیده
The polycrystalline Sn added Ni-Zn ferrites were prepared using the conventional sintering method. The monophasic nature of the samples was characterized using X-rays. The elastic behavior has been measured in the temperature range 80-410oC using the composite oscillator method. The values of Young’s and shear modulus are corrected to theoretical density using the method of Mackenzie method. The variation of Young’s and rigidity modulus with temperature follows Watchman’s equation and a linear equation respectively.
منابع مشابه
E-effect in Nickel-zinc Ferrites
A study of the dependence of elastic behaviour of polycrystalline mixed Ni-Zn ferrites of different compositions on temperature and magnetic field (AE-effect) has been made using a ultrasonic method. The variation of Young's modulus with temperature follows Wachtman's equation. The dependence of the Young's modulus on magnetic field is explained using a theoretical model suggesteds by Lewis and...
متن کاملTemperature dependence of core loss in cobalt substituted Ni-Zn-Cu ferrites
The temperature dependence of core loss in cobalt substituted Ni-Zn-Cu ferrites was investigated. Co ions are known to lead to a compensation of the magnetocrystalline anisotropy in Ni-Zn ferrites, at a temperature depending on the cobalt content and the Ni / Zn ratio. We observed similar behaviour in Ni-Zn-Cu and it was found that the core loss goes through a minimum around this magneto-crysta...
متن کاملINFLUENCE OF THE Zn2+ AND Cd2+ ION CONTENTS UPON THE NATURAL SPIN RESONANCE FREQUENCY IN Ni-Zn AND Ni-Cd FERRITES
— The influence of the Zn and Cd ion contents upon the natural spin resonance in Ni-Zn and Ni-Cd ferrites has been investigated. Previous experiments by other authors have shown that substituting Zn ions for Ni ions leads to a change of the total effective anisotropy field and consequently of the natural spin resonance frequency fi. ft measurements have been carried out by using a coaxial line ...
متن کاملInterfacial Dielectric Losses in Co-Doped Ni-Zn Ferrites
The temperature and fresuency dependence of tg8 and E' for Nk ~Ztb ferrites was studied in the 10'lo6 Hz frequency range and 20-200°C temperrhrre tange. The experimental curves exhibit aspects very dependent of composition. To verify Ulat interfacial losses, expected to appear in this type of system are compatible with the experimental results a calculation of the dielectric permittivity and di...