One-Step Preparation and Characterization of Zinc Phosphate Nanocrystals with Modified Surface
نویسندگان
چکیده
The surface-modified zinc phosphate (Zn3(PO4)2) nanocrystals were synthesized by a facile and efficient one-step ultrasonic-template-microwave (UTM) assisted route. The crystal structure, optical properties and morphologies of zinc phosphate nanocrystals were characterized by X-ray diffraction, Fourier transform infrared spectroscopy, Raman spectroscopy and transmission electron microscope. And the TEM image showed that the product had good dispersion with a particle size of 30 35 nm. The anti-corrosion function of anti-corrosive paint using zinc phosphate nanocrystals was researched and the experiment result showed that the salt atmosphere-resistant time was 158 h longer than that of zinc phosphate bulk materials on market. The performance of zinc phosphate nanocrystals with modified surface synthesized by one-step UTM assisted route was improved 63.2% compared with the bulk materials.
منابع مشابه
AN IMPROVEMENT TO THE ANTICORROSIVE PROPERTIES OF EPOXY POWDER COATING BY ZINC PHOSPHATE AND ZINC ALUMINUM PHOSPHATE PIGMENTS
Epoxy powder coatings containing zinc aluminum phosphate (ZAP) and zinc phosphate (ZP), which are the 2nd and 1st generation of phosphate-based pigments respectively, were applied to the surface of mild steel sheets. The anticorrosive performances of the coated samples were studied using electrochemical impedance spectroscopy (EIS). Cathodic disbonding resistance and the adhesion performance of...
متن کاملPreparation and Characterization of a Novel Biodegradable Epoxy Resin Modified with Epoxidized Oleic Acid
The goal of this research was to study the curing behavior and biodegradability DER 736 modified with epoxidized oleic acid. In this paper we demonstrate the efficient epoxidation of oleic acid with performic acid generated in situ from formic acid and hydrogen peroxide in the presence of H2SO4 as catalyst. The highest relative epoxy yield of 61% was achieved at 40 ͦC after 10 h. DER 736 modifie...
متن کاملPreparation of ZnO Nanocrystals with Desired Morphology from Coordination Polymers through a Solid-state Decomposition Route
One-dimensional (1D) coordination polymer, [Zn(4,4´-bpy)(H2O)4](ADC).4H2O (1) (4,4´-bpy = 4,4´-bipyridine and H2ADC = acetylenedicarboxylic acid), and three-dimensional (3D) metal-organic framework (MOF), Zn(ADC)2.(HTEA)2(2) (HTEA = triethylamine) were prepared at room temperature. The compounds were characterized by single-crystal X-ray diffraction and powder X-ray diffraction (PXRD) analyses....
متن کاملSynthesis of Zinc (II) Oxide Wurtzite Nano Crystals Via Zn (II) Minoxidil Nanocomposite As a New Precoursur
The study describes the synthesis and characterization of zinc(II) minoxidil nanocomposite (1). The reaction between zinc(II) acetate, minoxidil, {C9H15N5O=minoxidil=(2,4-diamino-6-piperidine-1-yl) pyrimidine N-oxide)} as a ligand and KI as bridging agent, in methanol at 60°C leads to the formation of nano-sized Zn(II) minoxidil nanocomposite, 1. Characterization of (1) was carried out by eleme...
متن کاملSynthesis and characterization of transition metal doped ZnSe/ZnS nanocrystals by a rapid photochemical method
In the present work, a one pot, rapid and room temperature photochemical Synthesis of transition metal (TM; Cu, Mn, Cr)-doped ZnSe/ZnS core/shell nanocrystals (NCs) was reported. FT-IR spectrum confirmed the capping of ZnSe by thioglycolic acid. XRD and TEM analysis demonstrated zinc blende phase NCs with an average size of around 3 and 5 nm for TM:ZnSe and TM:ZnSe/ZnS NCs, respectively. PL spe...
متن کامل