Pressure induced octahedral tilting distortion in Ba2YTaO6.
نویسندگان
چکیده
Herein we communicate the first example of a pressure induced octahedral tilting distortion in a double perovskite phase, which was observed during the structural characterization of Ba2YTaO6 using high-pressure synchrotron X-ray powder diffraction.
منابع مشابه
Polymorphism in NaSbO3: structure and bonding in metal oxides.
A new polymorph of NaSbO(3) has been synthesized at 10.5 GPa and 1150 degrees C in a uniaxial split sphere anvil type press (USSA-2000) and recovered back to ambient conditions. The high-pressure form of NaSbO(3) adopts an orthorhombically distorted perovskite structure, isostructural with CaTiO(3), GdFeO(3), and NaTaO(3). The space group is Pnma, and the unit cell dimensions are a = 5.43835(6)...
متن کاملStructure prediction of ordered and disordered multiple octahedral cation perovskites using SPuDS.
The software package SPuDS has previously been shown to accurately predict crystal structures of AMX(3) and A(1 - x)A'(x)MX(3) perovskites that have undergone octahedral tilting distortions. This paper describes the extension of this technique and its accuracy for A(2)MM'X(6) ordered double perovskites with the aristotype Fm\overline 3m cubic structure, as well as those that have undergone octa...
متن کاملJahn-Teller distortions, cation ordering and octahedral tilting in perovskites.
In transition metal oxides, preferential occupation of specific d orbitals on the transition metal ion can lead to the development of a long-range ordered pattern of occupied orbitals. This phenomenon, referred to as orbital ordering, is usually observed indirectly from the cooperative Jahn-Teller distortions (CJTDs) that result as a consequence of the orbital ordering. This paper examines the ...
متن کاملOctahedral tilting in cation-ordered perovskites--a group-theoretical analysis.
Group-theoretical methods are used to enumerate the structures of ordered perovskites, in which 1:2 and 1:3 ordering of B and B' cations is considered in combination with the ubiquitous BX6 (or B'X6) octahedral tilting. The cation ordering on the B-cation site is described by irreducible representations of the Pm3 m space group of the cubic aristotype: Lambda1 (k = 1/3,1/3,1/3) for the cation o...
متن کاملStructure for perovskites with layered ordering of A-site cations.
The structure of La(1/3)NbO3 is that of a perovskite with La3+ cations ordered into alternate layers of perovskite A-sites. This is the description of a tetragonal structure and yet the room-temperature structure shows an orthorhombic distortion. The structure of La(2/3)TiO3 shows similar features. It has been recognized only very recently that the orthorhombic distortion in both these compound...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 2 شماره
صفحات -
تاریخ انتشار 2006