Transformations of PTCDA structures on rutile TiO2 induced by thermal annealing and intermolecular forces
نویسندگان
چکیده
Transformations of molecular structures formed by perylene-3,4,9,10-tetracarboxylic dianhydride (PTCDA) molecules on a rutile TiO2(110) surface are studied with low-temperature scanning tunnelling microscopy. We demonstrate that metastable molecular assemblies transform into differently ordered structures either due to additional energy provided by thermal annealing or when the influence of intermolecular forces is increased by the enlarged amount of deposited molecules. Proper adjustment of molecular coverage and substrate temperature during deposition allows for fabrication of desired assemblies. Differences between PTCDA/TiO2(110) and PTCDA/TiO2(011) systems obtained through identical experimental procedures are discussed.
منابع مشابه
Effect of Annealing Temperature on Structural, Electrical and Optical Properties of TiO2 Nanopowder
TiO2 nanopowder is prepared by simple sol-gel method using starting material as titanium isopropoxide with methanol and annealed at 600°C, 700°C and 800°C for 1 hour in air. X-ray diffraction pattern revealed the presence of both anatase and rutile phase in TiO2 specimens annealed at different temperatures. It is observed that the content of rutile phase and crystallite size increases with incr...
متن کاملSTUDY OF ANNEALING TEMPERATURE VARIATION ON THE STRUCTURAL PROPERTIES OF DIP-COATED TiO2-SiO2 NANOSTRUCTURED FILMS
Abstract:In the present research, SiO2–TiO2 nanostructure films were successfully prepared on windshields using the sol–gel technique for photocatalytic applications. To prevent the thermal diffusion of the sodium ions from the glass to TiO2 films, the SiO2 layer was pre-coated on the glass by the sol–gel method. The substrates were dipped in the sol and withdrawn with the speed of 6cm/min-1 to...
متن کاملEffects of annealing temperature and method on structural and optical properties of TiO2 films prepared by RF magnetron sputtering at room temperature
TiO2 thin film was deposited on non-heated Si(1 0 0) substrate by RF magnetron sputtering. The as-deposited films were annealed by a conventional thermal annealing (CTA) and rapid thermal annealing (RTA) at 700 and 800 8C, and the effects of annealing temperature and method on optical properties of studied films were investigated by measuring the optical band gaps and FT-IR spectra. And we also...
متن کاملFabrication and Characterization of Rutile TiO2 Nanocrystals by Water Soluble Precursor
In this research, TiO2 nanoparticles were synthesized by a simple wet chemical method. TiCl4 was used as precursor in hydrogen peroxideand ethanol. The TiO2 nanoparticles were characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), electron dispersive spectroscopy (EDS) and UV-Vis spectrophotome...
متن کاملPreparation and Photocatalytic Property of TiO2 Columnar Nanostructure Films
The rutile TiO2 films with columnar nanostructure were prepared by combining the glancing angle deposition (GLAD) technique in magnetron sputtering system with the subsequent two-step annealing treatment. Experimental results showed that all the TiO2 films kept discrete columnar structures as the Ti films deposited by GLAD and accomplished the phase transition from Ti to rutile TiO2. Such TiO2 ...