Polydopamine-Coated Manganese Complex/Graphene Nanocomposite for Enhanced Electrocatalytic Activity Towards Oxygen Reduction
نویسندگان
چکیده
Platinum electrodes are commonly used electrocatalysts for oxygen reduction reactions (ORR) in fuel cells. However, this material is not economical due to its high cost and scarcity. We prepared an Mn(III) catalyst supported on graphene and further coated with polydopamine, resulting in superior ORR activity compared to the uncoated PDA structures. During ORR, a peak potential at 0.433 V was recorded, which is a significant shift compared to the uncoated material's -0.303 V (both versus SHE). All the materials reduced oxygen in a wide pH range via a four-electron pathway. Rotating disk electrode and rotating ring disk electrode studies of the polydopamine-coated material revealed ORR occurring via 4.14 and 4.00 electrons, respectively. A rate constant of 6.33 × 10(6) mol(-1)s(-1) was observed for the polydopamine-coated material-over 4.5 times greater than the uncoated nanocomposite and superior to those reported for similar carbon-supported metal catalysts. Simply integrating an inexpensive bioinspired polymer coating onto the Mn-graphene nanocomposite increased ORR performance significantly, with a peak potential shift of over +730 mV. This indicates that the material can reduce oxygen at a higher rate but with lower energy usage, revealing its excellent potential as an ORR electrocatalyst in fuel cells.
منابع مشابه
High Pt Loading on Polydopamine Functionalized Graphene as a High Performance Cathode Electrocatalyst for Proton Exchange Membrane Fuel Cells
Morphology and size of platinum nanoparticles are a crucial factor in improving their catalytic activity and stability. Here, we firstly report the synthesis of high loading Pt nanoparticles on polydopamine reduced Graphene. The loading concentration of Pt (nanoparticles) NPs on Graphene can be adjusted in the range of 60-70%.With the insertion of polydopamine between Graphene oxide sheets, sta...
متن کاملA hybrid of holey graphene and Mn3O4 and its oxygen reduction reaction performance.
A hybrid of holey graphene and Mn3O4 is prepared by a one-step process, in which the formation of a holey structure is accompanied with Mn3O4 nanoparticles through a high temperature reaction between graphene oxide sheets and KMnO4. Holey graphene and Mn3O4 collaboratively attributed to the enhanced catalytic activity and efficiency towards the oxygen reduction reaction.
متن کاملLayer-by-layer self-assembly for constructing a graphene/platinum nanoparticle three-dimensional hybrid nanostructure using ionic liquid as a linker.
In this report, we succeed in constructing a hybrid three-dimensional (3D) nanocomposite film by alternatively assembling the graphene nanosheets modified by ionic liquid (IL) and Pt nanoparticles (Pt NPs). In this strategy, an imidazolium salt-based ionic liquid (IS-IL)-functionalized graphene was synthesized by covalently binding 1-(3-aminopropyl)-3-methylimidazolium bromide onto graphene nan...
متن کاملPerformance comparison of graphene and graphene oxide-supported palladium nanoparticles as a highly efficient catalyst in oxygen reduction
In this work, the performance of graphene nanosheets (GNs) and graphene oxide (GO) nanosheets, as a support for palladium nanoparticles (PdNPs) toward oxygen reduction reaction (ORR), was studied. The graphene nanosheets were functionalized by a new and simple method. The PdNPs were synthesized on a glassy carbon electrode (GCE) modified with GNs or GO via a potentiostatic method; without using...
متن کاملDirect growth of flower-like manganese oxide on reduced graphene oxide towards efficient oxygen reduction reaction.
Three-dimensional manganese oxide is directly grown on reduced graphene oxide (RGO) sheets, exhibiting comparable catalytic activity, higher selectivity and better stability towards oxygen reduction reaction than those of the commercial Pt/XC-72 catalyst.
متن کامل