Preparation of layered double hydroxide films with different orientations on the opposite sides of a glass substrate by in situ hydrothermal crystallization.
نویسندگان
چکیده
MgAl-Layered double hydroxide (LDH) films with different orientations on the two sides of a glass substrate, one of which was modified with poly(vinyl alcohol), have been obtained by a one-step in situ hydrothermal crystallization method, and the growth mechanisms of the two films are discussed.
منابع مشابه
Crystallization Kinetics of Hydroxyapatite Nano-films on Stainless Steel Through a Sol-Gel Process
This article describes the preparation and analysis of nano hydroxyapatite (HA) films on stainless steel 316L through sol-gel technique. The process started with preparation of a nitrate and phosphate sol. After aging the sol for 24 h at room temperature a SS316 substrate was dip-coated and heat-treated at 350 to 450 °C for different times in air. The coating phase and structure on subs...
متن کاملPreparation and Characterization of Layered Silicate Polyethylene Terephthalate Nanocomposite by in Situ Polymerization
A series of experiments on the synthesis of poly (ethylene terephthalate) (PET)/organo-montmorillonite (MMT) nanocomposites were carried out in a pressurized reactor using alkyl ammonium exchanged smectite clays, (Closite 30B).Given the degradation of organoclay at high temperatures, the in situ polymerization process was carried out at mild temperatures ranging from 210 to 230°C for 40 minutes...
متن کاملFabrication of MgF2-SiO2 Nanocomposite Thin Films and Investigation of Their Optical and Hydrophobic Properties
In this research, MgF2-2%SiO2/MgF2 thin films were applied on a glass substrate. At first, MgF2 thin films with the optical thickness were deposited on the glass slide substrates. Then, MgF2-2%SiO2 thin films were deposited on the glass coated with MgF2 thin films. Finally, the nanocomposite thin films were surface treated by the PFTS solution. Characterization of the thin film was done by X-Ra...
متن کاملResidual Stress in Cu Sputtered Films on Glass Substrates at Different Substrate Temperatures
Copper films of 300 nm thickness deposited by planar magnetron sputtering on glass substrates, for substrate temperatures between 300 and 500 K, and deposition rate of 10 ?s?1. Microstructure of these films was obtained by X-ray diffraction, while the texture mode of diffractometer was used for stress measurement by the sin2? technique. The components of the stress tensor are obtained using mea...
متن کاملPreparation and proposed mechanism of ZnO Nanostructure Thin Film on Glass with Highest c-axis Orientation
In this paper, ZnO thin film is deposited on slide glass substrate using the sol-gel process. Presenting well-defined orientation of ZnO thin films Nanostructure were obtained by dip coating of zinc acetate dihydrate, monoethanolamine (MEA), de-ionized water and isopropanol alcohol. The annealed ZnO thin films were transparent ca 85-90% in visible range with an absorption edges at about 375 nm....
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 44 شماره
صفحات -
تاریخ انتشار 2009