Exposure Test on Two Surface Anticorrosion Technologies for Marine Concrete Structure
نویسندگان
چکیده
This paper is to study the effect of surface coating and silane hydrophobic agents for high performance concrete durability in a marine environment of tidal zone and splash zone by exposure test in JiaoZhou Bay. The results indicated that surface coating had good protection and coating quality after a 5-year period and the adhesive strength with concrete surface was more than 2.5 MPa. Surface coating can effectively improve chloride ion penetration resistance of concrete structures. The substrate concrete of specimen treated with silane had some chloride ion penetration, but compared with untreated concrete, chloride content of silane-treated concrete within 10 mm depth from surface was reduced by 43 and 67% in the tidal zone and the splash zone, respectively. Two surface anticorrosion measures technologies were effective in reducing the chloride erosion and improved the service life of marine concrete structure.
منابع مشابه
Durable Glass Fiber Reinforced Concrete with Supplimentary Cementitious Materials
Durability of concrete structure in marine environments is a big issue for many decades due to chloride attack. Chloride penetrates the concrete structure and accelerates the corrosion process of reinforcement which decreases the life of those structures. Also shrinkage cracks in concrete play main role for chloride penetration through concrete surface. Many researchers tried to find easy and ...
متن کاملEffect of Impressed Current on Bond Strength Between Steel Rebar and Concrete
The deterioration of bond strength between reinforcing steel and concrete as a result of impressed cathodic current with respect to the exposure time was investigated. A current in the magnitude of 3ma/ft2 (based on reinforcing rebar area) was used for a period of five years. Chemical analyses for sodium (Na+), potassium (K+) and chloride (Cl-) ions in concrete cylinders were performed as a fun...
متن کاملTime-Dependent Structural Behavior of Repaired Corroded RC Columns Located in a Marine Site
The chloride corrosion of reinforcing steel in reinforced concrete (RC) structures is a significant reason for premature deterioration and failure of RC structures in aggressive environments such as Persian Gulf region. This is one of the most important sources of engineering and economic problems in developed countries. So, the repair and maintenance of RC structures exposed to corrosive envir...
متن کاملOptimization of concrete structure mixture plan in marine environment using genetic algorithm
Today due to increasing development and importance of petroleum activities andmarine transport as well as due to the mining of seabed, building activities such as construction of docks, platforms and structures as those in coastal areas and oceans has increased significantly. Concrete strength as one of the most important necessary parameters for designing, depends on many factors such as mixtu...
متن کاملEvaluation of anticorrosion behavior of automotive electrocoating primers by the AC-DC-AC accelerated test method
A protective coating has been applied onto the phosphated panels using cathodic electrocoating in two different dry film thickness namely 8µm and 20µm. The corrosion resistance of cathodic electrocoatings has been studied using AC/DC/AC method. Twelve cycles of AC/DC/AC test were carried out on each sample which the DC voltage of the first 6 cycles were -4 V VS. Ag/AgCl @ 20 minutes followed by...
متن کامل