The thermal expansion coefficient of Al3Sc and Al3(Sc0:75X0:25), where X is Ti, Y, Zr or Hf, was measured by dilatometry between 25 and 1000 C. The measured value, ð16 1Þ 10 6 K , is constant between 25 and 900 C and insensitive to alloying element. Good agreement is found with a literature value determined from first-principle cal-
منابع مشابه
Role of silicon in accelerating the nucleation of Al3(Sc,Zr) precipitates in dilute Al–Sc–Zr alloys
The effects of adding 0.02 or 0.06 at.% Si to Al–0.06Sc–0.06Zr (at.%) are studied to determine the impact of Si on accelerating Al3(Sc,Zr) precipitation kinetics in dilute Al–Sc-based alloys. Precipitation in the 0.06 at.% Si alloy, measured by microhardness and atom-probe tomography (APT), is accelerated for aging times <4 h at 275 and 300 C, compared with the 0.02 at.% Si alloy. Experimental ...
متن کاملTHERMAL ANALYSIS AND KINETICS OF THE PRECIPITATION IN WROUGHT Al-Mg, Al-Mg-ScAND Al-Mg-Sc-Me (Me=Zr, Ti) ALLOYS
Precipitation behaviour of wrought Al-6Mg alloys with ternary scandium and quaternary zirconium and titanium has been studied. Hardness measurements and resistivity studies are employed to assess the precipitation behaviour of scandium doped Al-6Mg alloy without or with quaternary additions of zirconium and titanium. Further, the kinetics of precipitations are studied by differential scanning c...
متن کاملPrecipitation evolution in Al–0.1Sc, Al–0.1Zr and Al–0.1Sc–0.1Zr (at.%) alloys during isochronal aging
Precipitation strengthening is investigated in binary Al–0.1Sc, Al–0.1Zr and ternary Al–0.1Sc–0.1Zr (at.%) alloys aged isochronally between 200 and 600 C. Precipitation of Al3Sc (L12) commences between 200 and 250 C in Al–0.1Sc, reaching a 670 MPa peak microhardness at 325 C. For Al–0.1Zr, precipitation of Al3Zr (L12) initiates between 350 and 375 C, resulting in a 420 MPa peak microhardness at...
متن کاملMicrostructure of Al3Sc with ternary rare-earth additions
The microstructure of ternary L12-Al3(Sc1 yREy) intermetallics, where RE is one of the rare-earth elements selected from five light (La, Ce, Nd, Sm or Eu) or two heavy lanthanoids (Yb or Lu), was investigated as a function of RE concentration for 0.02 y 0.75. Alloys with light RE show two phases: L12-Al3(Sc,RE) and D019-Al3(RE,Sc) (or C11b-Al4(Eu,Sc)). Alloys with heavy RE exhibit a single L12A...
متن کاملMicrostructure of Al3Sc with ternary transition-metal additions
The microstructure of binary Al3Sc and ternary Al3(Sc1−yXy), where X is one of the transition metals from Group IIIA (Y), IVA (Ti, Zr or Hf) or VA (V, Nb or Ta), was investigated as a function of alloying element concentration for 0.1 y 0.75. Alloys with Group IIIA and IVA additions exhibited a single L12 solid-solution phase with some Kirkendall porosity. At the highest concentration studied, ...