The Evaluation of Flexural Strength of Composite Resin Materials with and without Fiber
نویسندگان
چکیده
The aim of the present study was to evaluate the effect of solutions, times of storage and reinforcement with fiber on the flexural strength of different composite materials. Nanofill and nanohybrid composite materials with and without fiber, a glass fiber and polyethylene fiber, were tested in the present study. 72 specimens (25×2×2 mm3) were prepared as following six groups; Group ECME: everStick Fibre / Clearfil Majesty Esthetics, Group EFU: ever Stick Fibre / Filtek Ultimate, Group RCME: Ribbond Fibre / Clearfil Majesty Esthetics, Group RFU: Ribbond Fibre / Filtek Ultimate, Group CME: Clearfil Majesty Esthetics, Group FU: Filtek Ultimate. The specimens were stored in distilled water and mouthwash and tested after 24 hours and 7 days. Data were analyzed using analysis of variance and Schefee test. It was found that the EFU group in distilled water for 24 hours had the highest flexural strength and the CME group in mouthwash for 7 days had the lowest flexural strength. The storage times and the solutions were not statistically significant factors affecting on the flexural strength. The mean flexural strength values of the RCME and the RFU groups were similar to the FU group.
منابع مشابه
(افزایش مقاومت خمشی کامپوزیتها توسط کشش الیاف (یادداشت فنی
In the present research work, the flexural modulus and strength of glass fiber-epoxy resin and carbon fiber-epoxy resin composites have been enhanced through fiber tension during curing of the polymeric resin. This study showed that the tension applied on the fibers increased the flexural modulus of the glass-epoxy composites up to 12% and the flexural strength up to 19%. The flexural modulus a...
متن کاملThe effect of different fiber reinforcements on flexural strength of provisional restorative resins: an in-vitro study
PURPOSE The aim of this study was to compare the flexural strength of polymethyl methacrylate (PMMA) and bis-acryl composite resin reinforced with polyethylene and glass fibers. MATERIALS AND METHODS Three groups of rectangular test specimens (n = 15) of each of the two resin/fiber reinforcement were prepared for flexural strength test and unreinforced group served as the control. Specimens w...
متن کاملساخت و بررسی خواص نانوکامپوزیت کربن/فنولیک با استفاده از روش پیرولیز پلیمر و تقویت آن با نانوذرات اکسید فلزی
Carbon fiber composite is one of the most important materials in aerospace engineering applications. For fabrication of this composite, optimum polymerization and carbonization cycles of phenolic resin were obtained [1]. Then, carbon/phenolic composite was fabricated by mixing different weight percentages of T700 carbon fiber with phenolic resin, and the flexural strength of specimens was exami...
متن کاملDevelopment of metal-resin composite restorative material. Part 4. Flexural strength and flexural modulus of metal-resin composite using Ag-In alloy particles as filler.
The flexural strength and flexural modulus of an experimental metal-resin composite, which used Ag-In alloy particle as the filler, were evaluated. The effect of acid treatment and heat treatment on the Ag-In alloy particle was investigated. The flexural strength of the experimental metal-resin composites ranged from 65.5 MPa to 91.0 MPa. The flexural strength of the metal-resin composite incre...
متن کاملComparative Evaluation of the Flexural Strength of Heat Polymerized Acrylic Resin with the Addition of 8% and 13% Aluminum Oxide Powder: An In-vitro Study
Introduction: Acrylic resins have been used successfully as denture bases. However, acrylic resin denture base materials are brittle and have poor strength and thermal conductivity. Therefore, it is essential to improve the flexural strength of heat polymerized acrylic resin. The present study aimed to evaluate and compare the flexural strength of heated polymerized acrylic res...