The Structure and Magnetic Properties of Co77Zr18W5 Melt-Spun Ribbons

نویسندگان

  • Shifeng Xu
  • Dan Xu
  • Zhipeng Hou
  • Jinbao Zhang
  • Feng Su
  • Liyuan Sun
  • Wenquan Wang
چکیده

Based on X-ray diffraction, microscopic and magnetic analysis, the structure and magnetic properties of Co77Zr18W5 melt-spun ribbons were studied in this paper. A new element to stabilize the metastable Co5Zr phase was found and the coercivity observed in Co-Zr alloys can be obviously enhanced by proper tungsten substitution. The Curie temperature of Co77Zr18W5 ribbons is 475 ̊C which suggests that W doped Co-Zr alloys may become an attractive candidate permanent magnets for practical applications in high temperature. Annealing of the Co77Zr18W5 ribbons results in a decrease of the coercivity which confirmed that the hard magnetic phase is Co5Zr phase in Co77Zr18W5 melt-spun ribbons.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

ساختار و خواص مغناطیسی آلیاژهای ‍‍CoFeSiB انجماد سریع یافته

The effects of metalloids Si(4-27 at%) and B(5-22 at%) on the structure and magnetic properties of melt spun cobalt based alloys containing 5at% Fe have been studied. XRD results revealed that in non-eutectic ternary CoFeSi and CoFeB alloys, the additions of Si or B, alone can not lead to full amorphization of melt spun ribbons. In quaternary CoFeSiB alloys, the total amounts of Si and B additi...

متن کامل

Effect of Joule-Heating Annealing on Giant Magnetoimpedance of Co64Fe4Ni2B19-xSi8Cr3Alx (x = 0, 1 and 2) Melt-Spun Ribbons

In this work, we have studied the influence of dc joule-heating thermal processing on the structure, magnetoimpedance (MI) and thermal properties of Co64Fe4Ni2B19-xSi8Cr3Alx (x = 0, 1, and 2) rapidly solidified melt-spun ribbons. The nanocrystallization process was carried out by the current annealing of as-spun samples at various current densities. As-spun and joule-heated samples were studied...

متن کامل

A comparative study of magnetostrictive strain in Pr3Fe24.75Co2.75Ti1.5-ingot and Pr3Fe24.75Co2.75Ti1.5-melt spun

In this work, the structural and magnetic properties of ingot and melt-spun Pr3Fe24.75Co2.75Ti1.5 compounds have been investigated. The structural characterization of the compounds, by X-ray powder diffraction, is evidenced for a monoclinic Nd3(Fe,Ti)29-type structure (A2/m space group). A 2-type FOMP have been observed in the magnetic AC susceptibility curves of the ingot and melt-spun compoun...

متن کامل

Dip coating of silica layer on melt-spun Finemet ribbons: surface morphology and electrical resistivity changes

In this study, melt-spun Finemet ribbons were coated by a thin layer of SiO2 using dip coating method. Amorphous ribbon prepared by melt spinning method and dip coating were done by using a solution of tetraethylen orthosilicate as a SiO2 precursor, ethanol as solvent and distilled water for hydrolysis. Different thicknesses of SiO2 layer, namely 304, 349, 451, 526 and 970 nm were obtained prop...

متن کامل

Introducing and investigating structural and magnetic properties of ribbons Co68.5-xFe4WxSi16.5B11 (x = 0.8, 2) in amorphous and crystalline states

In this study, for the first time, cobalt base ribbons were made by adding two different amounts of tungsten with Co67.7Fe4W0.8Si16.5B11 and Co66.5Fe4W2 Si16.5B11 compounds by melt spinning in the water. The pattern of  X-ray diffraction taken from these ribbons shows that these magnetic ribbons are amorphous. By using thermal analysis curves, taken from the ribbons, crystallization temperature...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2013