Influence of Uron Resins on the Performance of Uf Resins as Adhesives for Plywood
نویسندگان
چکیده
Uron resin, a kind of urea-formaldehyde (UF) resin containing much more uron structure, were prepared. Several modi ed UF resins were obtained from mixing uron resins with normal UF resins as well as synthesizing UF resin with uron resin as raw material. is work demonstrated that the introducing of the uron structure reduced free formaldehyde content of UF resin and formaldehyde emission levels in bonded plywood panels signi cantly, the former were reduced by 76% and 84% in the latter. e synthesis time of uron resin can be shortened to 8 hours. e test result of free formaldehyde content, formaldehyde emission levels and bond strength indicated that specimen of 20 parts uron resin synthesized in 8 hours mixed with 100 parts UF resins (F/U molar ratio of 1.3) had a potential advantage to industrial application. e bene cial e ect of uron resin on the performance of UF resin can be attributed to the opening of uron cycle structure and the following reaction with free formaldehyde and its oligomeric glycol forms.
منابع مشابه
Low Mole Ratio UF and UMF Resins Entailing Uron-Type Methylene-Ether Groups and their Low Formaldehyde Emission Potentials
The previous study on low mole ratio urea-formaldehyde (UF) and ureamelamine–formaldehyde (UMF) resins synthesized in the typical way as particleboard binders was repeated with the inclusion of a strong acidic reaction step at a mole ratio of 2.7 in the beginning of the resin synthesis procedure. The resulting UF and UMF resins showed longer storageand pot-lives, longer gel times, and the parti...
متن کاملEffects of Melamine Addition Stage on the Performance and Curing Behavior of Melamine-Urea-Formaldehyde (MUF) Resin
Three formaldehyde-based resins were prepared: urea-formaldehyde (UF) resin without melamine modifier (named UF0 resin) and melamineurea-formaldehyde (MUF) resins with melamine modifier added at two different synthesis stages (named MUF1 resin and MUF2 resin). The effects of the melamine addition stage on the performance and curing behavior of MUF resin were studied. Three-ply plywood bonded by...
متن کاملMelamine-modified urea formaldehyde resin for bonding particleboards
For the development of a cost-effective melamine-modified urea formaldehyde resin (MUF), the study evaluated the effects of reaction pH and melamine content on resin properties and bond performance of the MUF resin adhesive systems. Eight resins, each with three replicates, were prepared in a factorial experiment that included two formulation variables: two reaction pHs (i.e., 4.5 and 8.0) and ...
متن کاملLow Mole Ratio Urea–Melamine–Formaldehyde Resins Entailing Increased Methylene-Ether Group Contents and Their Formaldehyde Emission Potentials of Wood Composite Boards
A previous study of synthesizing low mole ratio urea–formaldehyde (UF) and urea–melamine–formaldehyde (UMF) resins, which included an acidic reaction step at the beginning of the typical resin synthesis procedure to obtain higher uron-type methylene–ether group contents, was repeated with the acidic reaction step extended to a higher viscosity. Compared to previous resins, the synthesized resin...
متن کاملPreparation and Characterization of a Phenol-formaldehyde Resin Adhesive Obtained From Bio-ethanol Production Residue
Phenol formaldehyde (PF) resins are widely used as wood adhesives in the industrial production of exterior-grade plywood panels, oriented strand board panels and particleboards due to their superior performance including high bonding strength, heat resistance, excellent water resistance and chemical stability1. However, phenol, one raw material for the synthesis of PF resins, is a petroleum-bas...