HITPERM soft-magnetic underlayers for perpendicular thin film media

نویسندگان

  • S. Kumar
  • D. E. Laughlin
چکیده

A class of nanocrystalline alloys, HITPERM ~Fe, Co!–M–B–Cu (M5Zr,Hf,Nb, etc.! found to exhibit excellent soft-magnetic properties is being studied for use as a soft-magnetic underlayer for perpendicular recording media. Previously, we reported that HITPERM films of ;100 nm thickness sputtered at room temperature ~RT! and at ;2.3 W/cm power density had exhibited an amorphous microstructure, which had turned mixed nanocrystalline when prepared at ;250 °C. However, nanoparticles of FeCo have now been crystallized even at RT without the application of heat, by increasing the sputtering power density to ;4.5 W/cm. This dramatically improved the 4pM s while still maintaining a low coercivity. There was a further slight increase in the 4pM s at ;6.8 W/cm. Moreover, these soft-magnetic properties were maintained even when the substrate temperature was subsequently raised to ;250 °C. Transmission electron microscopy studies showed the presence of relatively small nanocrystals of the ferromagnetic a8-FeCo ~or a-FeCo! phase alone, for both sets of films. Previously, we had reported that the CoCrPt magnetic layer grew with a strong ~00"2! texture on amorphous HITPERM. We have now seen that with a thin Ti intermediate layer ~;5 nm! the CoCrPt layer maintained a strong ~00"2! texture even on the nanocrystalline HITPERM. Thus, due to their particular nanocrystalline nature, these HITPERM films exhibit much better soft-magnetic properties, while still leading to strong ~00"2! texture on the CoCrPt magnetic layer. © 2003 American Institute of Physics. @DOI: 10.1063/1.1558091#

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Microstructure and magnetic properties of very" thin CoCr films deposited on different underlayers by if-sputtering

Very thin CoCr films deposited on different underlayers on glass disk substrates were studied by the magneto-optic Kerr effect, VSM, torque magnetometcy and TEM selected area diffraction. Square or near square perpendicular loops were obtained from Co/Ti , CoCr/Au: CoCr/AI, CoCr/C and CoCr/Si films. TEM SAD study revealed that the crystalline structure is a key factor determining the magnetic a...

متن کامل

New highly oriented soft magnetic underlayer structures for perpendicular recording

Highly oriented soft underlayers with face-centered-cubic ~fcc! phase Co, Co alloy, and composite NiFe/Co film structures have been epitaxially grown on single crystal Si wafers by sputter deposition. The epitaxial orientation relationships have been determined by x-ray diffraction and transmission electron microscopy. It was found that the soft underlayer magnetic properties can be modified in...

متن کامل

MgO seed layers for CoCrPt/Cr longitudinal magnetic recording media

Sputter deposited MgO thin films with the B1 crystal structure and ~002! film texture are used as seed layers to improve the texture and magnetic properties of the CoCrPt/Cr magnetic thin films on glass substrates for longitudinal recording. The desired ~002! textured Cr underlayers are usually obtained by sputtering Cr onto heated substrates. However, it is found that the MgO seed layers can i...

متن کامل

Magnetic and structural characterization and ferromagnetic resonance study of thin film HITPERM soft magnetic materials for data storage applications

HITPERM/SiO2 single and multilayer thin films have been produced using a target composition of (Fe70Co30)88Zr7B4Cu1 . The as-deposited HITPERM film contains small bcc ~or B2! nanocrystals of volume fraction less than 10% surrounded by an amorphous matrix. The lattice parameter of the nanocrystal is about 5% larger than an equilibrium FeCo phase. The saturation induction determined from FMR meas...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2002