Characterization of Bis-Acryl Composite Resins for Provisional Restorations.

نویسندگان

  • Júlia K Schwantz
  • Aline Oliveira-Ogliari
  • Carine T Meereis
  • Fernanda B Leal
  • Fabrício A Ogliari
  • Rafael R Moraes
چکیده

This study investigated the in vitro performance of the commercial bis-acryl composite resins Systemp C&B II (SYS, Ivoclar Vivadent), Protemp 4 (PT4, 3M ESPE), Structur 2C (ST2, Voco) and ProviPlast (PVP, Biodinamica). Characterization involved optical (color stability, translucency parameter, fluorescence), surface (roughness, morphology and elemental composition), physical-chemical (viscosity, polymerization kinetics) and mechanical analyses (Poisson ratio, biaxial flexural strength, flexural modulus). Most tests were carried out after 24 h, but optical and mechanical analyses were carried out after storage in water at 37 °C for 1, 15, and 30 days. Data were statistically analyzed (a=0.05). Most results were material dependent. SYS and PT4 showed stability in color and translucency over time. All materials had similar or higher fluorescence than human enamel. SC2 and PVP showed rougher surfaces than the other bis-acryl composites. Smaller filler particles were observed on the surface of PT4 and PVP compared with the coarser particles from ST2 and SYS. Viscosity readings indicated a thixotropic behavior for all tested materials. SYS had the lowest and PT4 the highest degree of C=C conversion after 10 min. In the polymerization kinetics, PT4 had the highest maximum polymerization rate and reached earlier the transition between polymerization autoacceleration and autodeceleration. PT4 and SYS had significantly higher flexural strength and modulus than ST2 and PVP for most storage times. Results for Poisson ratio varied between materials. Longer storage periods were generally associated with higher frequency of catastrophic failures in the flexural tests. In conclusion, the performance of bis-acryl composite resins varied largely among materials.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

The effect of different fiber reinforcements on flexural strength of provisional restorative resins: an in-vitro study

PURPOSE The aim of this study was to compare the flexural strength of polymethyl methacrylate (PMMA) and bis-acryl composite resin reinforced with polyethylene and glass fibers. MATERIALS AND METHODS Three groups of rectangular test specimens (n = 15) of each of the two resin/fiber reinforcement were prepared for flexural strength test and unreinforced group served as the control. Specimens w...

متن کامل

An Investigation into the Integrity of Fit of Provisional Crowns made over a Dental Implant Analogue Using Two Current Proprietary Provisional Crown Materials Compared to a Proprietary ‘Snap On’ Provisional Core

The aim of this study was to investigate the marginal accuracy of three currently used methods of direct provisional crown construction for the accuracy of marginal fit during in vitro fabrication. Three groups of provisional crowns were investigated using a modified McLean and von Fraunhofer technique. Proprietary provisional crown coping modified to tooth shape with a Bis-acryl temporary mate...

متن کامل

In vitro color and roughness stability of different temporary restorative materials.

OBJECTIVE The aim of this study was to evaluate the effects of staining solutions on the color stability and roughness of different provisional resin material. MATERIAL AND METHODS Three different materials were tested (two polymethylmethacrylate and one bis-acryl composite resins) in cola and coffee and for 1 and 4 weeks. 240 specimens were used - half of them polished and other half not. Co...

متن کامل

In Vitro Fit and Cementation Resistance of Provisional Crowns for Single Implant-Supported Restorations.

This study aimed to verify marginal fit and the effect of cement film thickness standardization on retention of provisional crowns made with prefabricated acrylic cylinders on abutments, using two temporary luting agents subjected or not to mechanical cycling. Provisional crowns were made from bis-acryl (Luxatemp Fluorescence) or methyl methacrylate (Duralay) resins on acrylic cylinders and mar...

متن کامل

In vitro comparative evaluation of mechanical properties of temporary restorative materials used in fixed partial denture

INTRODUCTION Materials used to fabricate provisional restorations can be classified as acrylics or resin composites. Provisional crows can be either prefabricated or custom made. ACRYLICS These materials have been used to fabricate provisional restorations since the 1930s and usually available as powder and liquid. They are the most commonly used materials today for both single-unit and multi...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Brazilian dental journal

دوره 28 3  شماره 

صفحات  -

تاریخ انتشار 2017