Porous Ba Ferrite Prepared from Wood Template
نویسندگان
چکیده
Ba ferrite materials with porous microstructures were prepared from a natural cedar wood template in order to investigate new electromagnetic shielding materials. The wood templates were infiltrated with barium nitrate and iron nitrate solutions (molar ratio = 1:12) and dried to form ferrite gel, then, they were sintered in air at a temperature between 800 °C and 1400 °C. The 1-dimensional porous structures were retained after sintering and the pore size was approximately 10–20 μm. These ferrites show large coercive force and anisotropy field. The largest coercive force was obtained for the specimen sintered at 800 °C.
منابع مشابه
Synthesis of porous CdO sheet-like nanostructure based on soft template model and its application in dye pollutants adsorption
In this work, the synthesis of porous structure of cadmium oxide with multilayered sheet-like morphology in nano-meter size using adipic acid as soft template by solvothermal/thermal decomposition process is reported. Chemical analyses exhibited that the formation of porous sheet-like structure is originated from bidentate coordination mode of adipate units to Cd-center. It was found that the c...
متن کاملWood Nanotechnologies for Transparency, Fire Retardancy and Liquid Separation
In this thesis, wood nanotechnologies for transparent, fire-retardant and hydrophobic/lipophilic wood have been developed. There are two main parts; wood template preparation/processing concepts and materials design using these templates. In the wood template processing part, highly porous nanostructured wood templates are prepared. Relationships between processes and material structures are st...
متن کاملSynthesis of porous CdO sheet-like nanostructure based on soft template model and its application in dye pollutants adsorption
In this work, the synthesis of porous structure of cadmium oxide with multilayered sheet-like morphology in nano-meter size using adipic acid as soft template by solvothermal/thermal decomposition process is reported. Chemical analyses exhibited that the formation of porous sheet-like structure is originated from bidentate coordination mode of adipate units to Cd-center. It was found that the c...
متن کاملSynthesis and Characterization of Hierarchically Porous Silica with Poplar Tissue as Template with Assistance of Supercritical Co2
Hierarchically porous silica samples, ranging from mesopores to macropores, were prepared by “nanoscale casting using supercritical (SC) fluids” (NCSCF) technology and bionics, achieving a biomineralization process in an environmentally friendly and efficient way. These wood-templated SiO2 samples, having special hierarchical pore sizes from 3.3 nm up to 50 μm, were obtained with SC-CO2 precurs...
متن کاملRoom Temperature Methanol Sensor Based on Ferrite Cobalt (CoFe2O4) Porous Nanoparticles
In this work, porous nanoparticles of ferrite cobalt were prepared by dissolving CoCl2.6H2O and FeCl3 in ethylene glycol in a hydrothermal process. Using ethylene glycol instead of DI water as a solvent would cause to provide porous structure of ferrite cobalt. 0.05 ml of colloidal fluid of fabricated nanostructure was injected on interdigitated electrodes (IDE) on a printed circuit board (PCB)...
متن کامل