Structure-property relations of co-doped bismuth layer-structured Bi3.25La0.75(Ti1-xMox)3O12 ceramics
نویسندگان
چکیده
In this work, the fabrication and investigation of substituting higher-valence Mo6+ for Ti4+ ion on the B-site of La3+-doped Bi4Ti3O12 [BLT] structure to form Bi3.25La0.75(Ti1-xMox)3O12 [BLTM] (when x = 0, 0.01, 0.03, 0.05 0.07, 0.09, and 0.10) ceramics were carried out. X-ray diffraction patterns of BLTM ceramics indicated an orthorhombic structure with lattice distortion, especially with a higher concentration of a MoO3 dopant. Microstructural investigation showed that all ceramics composed mainly of plate-like grains. An increase in MoO3 doping content increased the length and thickness of the grain but reduced the density of the ceramics. Electrical conductivity was found to decrease, while the dielectric constant increased with Mo6+ doping concentration. Ferroelectric properties were found to be improved with increasing MoO3 content and were optimized at x = 0.1.
منابع مشابه
Composition-driven structural phase transitions in rare-earth-doped BiFeO3 ceramics: a review.
Bismuth ferrite suffers from high leakage currents and the presence of a complex incommensurate spin cycloidal magnetic ordering, which has limited its commercial viability and has led researchers to investigate the functionality of doped BiFeO3 ceramics. In particular, the substitution of rare earths onto the Bi(3+) site of the perovskite lattice have been shown to lead to improved functional ...
متن کاملPreparation and Study of Bismuth Oxide Doped and co-Doped with Cobalt(III) and Holmium(III) via Sol-Gel Method
In this research work the solid-solutions of (Bi2O3)1-x (Co2O3)x, [x= 0.05, 0.1] (1), (Bi2O3)1-x (Ho2O3) x, [x= 0.025, 0.05] (2), and (Bi2O3)1-x-y (Co2O3)x (Ho2O3)y</su...
متن کاملStructural Investigation, Physical and Optical Properties of Mixed Alkali Bismuth Borate Glasses
Lead free, eco-friendly bismuth borate glasses doped with alkali oxides of composition xLi2O+(30-x)Na2O+55B2O3+15Bi2O3 (x = 5,10,15,20,25) were prepared by melt quenching technique. Amorphous nature of glasses was confirmed by X-ray diffraction. Density measurements were carried out at room temperature by standard principle of Archimedes with Xylene as an immersion liquid. The non-linear ...
متن کاملMullite interaction with bismuth oxide from minerals and sol-gel processes
The high temperature treatment of kaolinite-muscovite alternate layers doped by bismuth oxide was studied by TGA and DTA, X ray diffraction, and electron microscopy (SEM). Thermal analyses shows that the two main transformation stages are the dehydroxylation of phyllosilicates and the structural reorganization of the whole assembly. During dehydroxylation, a progressive decrease of the structur...
متن کامل