Brief data overview of differently heat treated binder jet printed samples made from argon atomized alloy 625 powder
نویسندگان
چکیده
Powder bed binder jet printing (BJP) is an additive manufacturing method in which powder is deposited layer-by-layer and selectively joined in each layer with binder. The data presented here relates to the characterization of the as-received feedstock powder, BJP processing parameters, sample preparation and sintering profile ("Effect of solutionizing and aging on the microstructure and mechanical properties of powder bed binder jet printed nickel-based superalloy 625" (A. Mostafaei, Y. Behnamian, Y.L. Krimer, E.L. Stevens, J.L. Luo, M. Chmielus, 2016) [1], "Powder bed binder jet printed alloy 625: densification, microstructure and mechanical properties" (A. Mostafaei, E. Stevens, E. Hughes, S. Biery, C. Hilla, M. Chmielus, 2016) [2]). The data presented here relates to the characterization of the as-received feedstock powder, BJP processing parameters, sample preparation and sintering profile. Effect of post heat treatments including solutionizing and aging on the microstructure and mechanical properties of powder bed binder jet printed nickel-based superalloy 625 were compared to that of sintered samples.
منابع مشابه
Data on the densification during sintering of binder jet printed samples made from water- and gas-atomized alloy 625 powders
Binder jet printing (BJP) is a metal additive manufacturing method that manufactures parts with complex geometry by depositing powder layer-by-layer, selectively joining particles in each layer with a polymeric binder and finally curing the binder. After the printing process, the parts still in the powder bed must be sintered to achieve full densification (A. Mostafaei, Y. Behnamian, Y.L. Krime...
متن کاملPrinted 3D coloured objects: 3D ink-jet prints colour properties and colour stability
3D ink-jet printing is an additive, powder-based rapid prototyping (RP) process. The 3D printing process described in this overview has been developed by ZCorporation and is based on an ink-jet printing technique. The 3D computer models, created by 3D scanning or in 3D CAD modelling software, are built layer by layer from the basic materials of powder and binders. Due to the basic build princip...
متن کاملEvaluation of Flank Wear of Iron-rich Binder Carbide Cutting Tool in Turning of Titanium Alloy
Despite the fact that Titanium material has been considered as difficult to cut material, its usage has been increasing day by day in all engineering sectors; wherever criticality is encountered. Many studies are going on in view of increasing tool life at high cutting speed to improve productivity. In this study, attempt has been made to see the effect of iron as a partial substitution along ...
متن کاملStructure, Properties, and In Vitro Behavior of Heat-Treated Calcium Sulfate Scaffolds Fabricated by 3D Printing
The ability of inkjet-based 3D printing (3DP) to fabricate biocompatible ceramics has made it one of the most favorable techniques to generate bone tissue engineering (BTE) scaffolds. Calcium sulfates exhibit various beneficial characteristics, and they can be used as a promising biomaterial in BTE. However, low mechanical performance caused by the brittle character of ceramic materials is the ...
متن کاملEFFECTS OF REINFORCEMENT VOLUME FRACTION, REINFORCEMENT SIZE AND SOLUTION HEAT TREATMENT ON THE MICROSTRUCTURE OF THE TWO DIFFERENTLY PROCESSED A35&SICPCOMOSITES
In this study different volume fractions of SiC particles of various sizes were introduced into the semisolid A356 aluminum alloy by a mechanical stirrer. Then the slurry was poured into a permanent die of certain dimensions either when the metal alloy was partially solid (semisolid-semisolid or SS route) or after reheating to above the liquidus temperature of the alloy (semisolid-liquid or SL ...
متن کامل