AE Feature Analysis on Welding Crack Defects of HG70 Steel Used by Truck Crane
نویسندگان
چکیده
In present paper, using Acoustic Emission (AE) as a ultrasonic technique, Welding crack has been investigated on the HG70 steel used by truck crane during three-point bending test was carried out. The study shows that the activity of AE increases greatly during the welding crack initiates and propagates, and the distributing range of AE characteristic parameters can be fixed. AE signals of welding crack initiation and expansion are typical sudden signals which have a different spectrum energy distribution range with that of unstable crack propagation.
منابع مشابه
Nondestructive Evaluation of Welding Crack Defects in Structural Component Of Track Crane Using Acoustic Emission Technique
On-line defects detection of structural component of track crane such as crane boom, outriggers, turntable and vehicle frame, is a difficult problem of nondestructive testing (NDT). In the present study, the usefulness of acoustic emission (AE) measurements for the detection of welding crack defects in the specimen made of HG70 steel, which is widely used for manufacturing structural component ...
متن کاملAcoustic Emission Mechanism and Source Modeling of Dynamic Crack Detection in Steel Structure
Cracks are dangerous and frequently observed defects in steel structures. Therefore, the understanding of the mechanism of crack is very important to structure safety. Although the mechanism of static crack has been widely studied by researchers, the mechanism of dynamic crack has been left out and seldom been discussed. In this paper, a modeling method for acoustic emission (AE) source of dyna...
متن کاملResearch on Cold Crack Sensitivity of High- Strength Wear-resistant Steel Nm360 after Welding
Article history: Received: 21.04.2014. Received in revised form: 02.07.2014. Accepted: 14.07.2014. Due to the high amount of carbon and diffusible hydrogen, high-strength wear-resistant steel NM360, which is widely used on excavating machinery, always tends to develop cold crack after welding. Heat affected zone (HAZ) is the weakest part in a welding joint and is the most probable location for ...
متن کاملDetection of crack growth in rail steel using acoustic emission
Increased traffic speeds and axle loads on modern railways enhance rail track degradation. To eliminate track failure due to rail defects, a condition monitoring system requires methods for the early detection of defects which grow in service. Acoustic emission (AE) monitoring is the only non-destructive technique which might be applied online to study the defect growth under traffic loading. H...
متن کاملVulnerability Assessment of Steel Structures in District 12 of Mashhad City and Prioritizing the Welding Defects Using the Analytic Hierarchy Process
Recently, steel structures have been accounted for a large percentage of the buildings due to their advantages such as higher execution speed and easier construction. In steel structures, welded joints are commonly used and their quality plays a key role in stability of buildings under applied loads. Hence, to increase resiliency of welded steel structures against natural hazards, welded joints...
متن کامل