Stacking Faults in Ca(OH)2 Produced by Vapour Phase Hydration
نویسنده
چکیده
The diffraction profiles of a thin single crystal with stacking faults were calculated with the theory of diffraction of a one-dimensionally disordered crystal (Kakinoki, Komura, Allegra) by including the effect of crystallite thickness. The results hold for generalized close packed structures. An application to calcium hydroxide is discussed: the stacking faults significantly contribute to the disorder of poorly crystalline forms of Ca(OH)2 produced by reaction of calcium oxide with water vapour at room temperature.
منابع مشابه
Results of X-ray investigations on hydration products of cementitious materials using special specimen holders and preparation techniques
Hydration products of calcium silicates and calcium aluminates often are difficult to identify by X-ray methods. In this study the hydration products of the aluminate phase especially under the influence of additional chloride ions were studied. Special X-ray measurement conditions must be applied for accurate identification including 1. In situ control of relative humidity 2. Exclusion of CO2 ...
متن کاملInelastic neutron scattering investigation of hydrating tricalcium and dicalcium silicate mixture pastes: Ca(OH)2 formation and evolution of strength
The hydration of controlled tricalcium and dicalcium silicate mixtures was investigated using inelastic neutron scattering. The amount of Ca(OH)2 produced by each mixture was quantified based on the vibrational mode at approximately 41 meV. The results of compressive strength testing correlate with the amount of Ca(OH)2 produced and with previous results from quasielastic neutron scattering. Th...
متن کاملStacking - fault energies in simple metals : applications to BCC metals
We present a general method for calculating the stacking-fault energy in simple metals, and then we apply this to the ( 1 1 2 ) faults in body-centred cubic (BCC) metals. Our method contains no approximations for a given wavenumber characteristic (or equivalently the pair potential). Our results show that metastable faults do indeed exist in the simple BCC metals (Li, Na. K, Rb, Cs, Ca. Sr, Ba)...
متن کاملCatalytic hydride vapour phase epitaxy growth of GaN nanowires.
Catalytic growth of GaN nanowires by hydride vapour phase epitaxy is demonstrated. Nickel-gold was used as a catalyst. Nanowire growth was limited to areas patterned with catalyst. Characterization of the nanowires with transmission electron microscopy, x-ray diffraction, and low temperature photoluminescence shows that the nanowires are stoichiometric 2H-GaN single crystals growing in the [000...
متن کاملThe Hydration Products of a Refractory Calcium Aluminate Cement at Low Temperatures
Calcium aluminates (CA) are the most important hydraulically setting cements used for preparing refractory castables, because they develop high strength at very early ages after placements. The anhydrous phases of this kind of cements are CA, CA2 and traces of C12A7 and alpha-alumina. The major hydraulic phase in all of the CA cements including ciment fondu...