Modeling of TiAl Alloy Grating by Investment Casting
نویسندگان
چکیده
The investment casting of TiAl alloys has become the most promising cost-effective technique for manufacturing TiAl components. This study aimed to investigate a series of problems associated with the investment casting of TiAl alloys. The mold filling and solidification of this casting model were numerically simulated using ProCAST. Shrinkage porosity was quantitatively predicted by a built-in feeding criterion. The results obtained from the numerical simulations were compared with experiments, which were carried out on Vacuum Skull Furnace using an investment block mold. The investment casting of TiAl grating was conducted for verifying the correctness and feasibility of the proposed method. The tensile test results indicated that, at room temperature, the tensile strength and elongation were approximately 675 MPa and 1.7%, respectively. The microstructure and mechanical property of the investment cast TiAl alloy were discussed.
منابع مشابه
Multiscale modeling for the prediction of casting defects in investment cast aluminum alloys
Macroscopic modeling of heat transfer and fluid flow is now routinely used for the prediction of macroscopic defects in castings, while microscopic models are used to investigate the effects of alloy changes on typical microstructures. By combining these two levels of modeling it is possible to simulate the casting process over a wider range of spatial and temporal scales. This paper presents a...
متن کاملTiAl-BASED ALLOYS: PRESENT STATUS AND FUTURE PERSPECTIVES
Intermetallic TiAl-based alloys represent an important class of high temperature structural materials providing a unique set of physical and mechanical properties that can lead to substantial payoffs in aircraft engines, industrial gas turbines and automotive industry. The present status and future perspectives of TiAl-based alloys are reviewed from the point of view of alloy design, processing...
متن کاملStudying the Effect of Productive Factors on Synthesis of Anostructure Tial (Γ) Alloy By Mechanical Alloying
In this research, the Planetary mill was used for mechanical alloying (MA) of Ti and Alpowder mixture with equal at% (Ti50Al50). The effect of various factors, such as process control agent(PCA), speed of rotation of vial and ball-to-powder weight ratio, on process were studied and the bestcondition to synthesis the alloy was determined. Study on X-ray diffraction (XRD) patterns showedthat at p...
متن کاملSynthesis of Nanostructure Ti-45Al-5Cr Alloy by Mechanical Alloying and Study the Effect of Cr Addition on Microstructure of TiAl Alloy
In this work, mechanical alloying was employed to produce Ti-50Al and Ti-45Al-5Cr (at%) alloys. Alloying was performed in a planetary mill and the alloying time varying from 5 to 70h. Characterization of the powder mixture was performed by X-ray diffraction (XRD), SEM analyses and DTA test, during mechanical alloying and after annealing at 1100°c in vacuum oven. The results showed, after 50h of...
متن کاملPlatinum Investment Casting , Part II : Alloy
Two widely used jewellery investment casting alloys (platinum with 5 wt% ruthenium (Pt-5Ru) and platinum with 5 wt% cobalt (Pt-5Co)) suffer from poor castability and other drawbacks. In this work thermodynamic calculations of alloy properties were employed to optimise the alloy compositions. Segregation behaviour appeared to be important for the melting range. Scheil simulations were used to si...
متن کامل