Intrinsic Properties of Fe-Substituted Magnets

نویسنده

  • P. Manchanda
چکیده

School of Basic Sciences, Indian Institute of Technology, Mandi, Himachal Pradesh, India Department of Physics and Astronomy and NCMN, University of Nebraska, Lincoln, NE 68588 USA Department of Mechanical and Materials Engineering, University of Nebraska, Lincoln, NE 68588 USA Department of Mechanical and Industrial Engineering, University of Massachusetts, Amherst, MA 01003 USA Arnold Magnetic Technologies, Rochester, NY 14625 USA Department of Applied Physics and Applied Mathematics, Columbia University, New York, NY 10027 USA Department of Chemical Engineering, Northeastern University, Boston, MA 02115 USA

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effect of Post-Sintering Annealing Treatment on Magnetic Properties of Some Nd Fe b Based Magnets

Effects of post-sintering annealing treatment between 300 and 1000ºC for up to 8 hrs time periods followed by either furnace cooling (FC) or air-cooling (AC) on the hard magnetic properties of some Nd-Fe-B based sintered magnets was investigated. It was shown that the intrinsic coercivity (Hci), second quadrant demagnetization loop shape and thus the energy density (BH)max varied considerably a...

متن کامل

High performance Nd-Fe-B permanent magnets without critical elements

Scanning electron microscopy, and magnetization measurements reveal that as cast (Nd1 xCex)2Fe14B alloys contain significant amounts of a-Fe that can be dramatically reduced by annealing the alloys at 1000 C for 3 days. The room temperature intrinsic coercivity, Hci, of (Nd0.8Ce0.2)2.2Fe14B melt spun ribbons was found to be 11 kOe, which is ~32e~10% higher in comparison to that of Nd2Fe14B (Hci...

متن کامل

Permanent magnets and hard magnetic materials

This review deals with the definition and development of hard magnetic materials with special emphasis on more recent developments in this field. After discussing the fundamental properties of all hard magnetic materials, based on the intrinsic and extrinsic properties, some remarks on the history of hard magnetic materials and permanent magnets are given. The important hard ferrites are only b...

متن کامل

Effect of Fe, Cu, Zr, and Ti on the Magnetic Properties of SmCo-1 : 7 Magnets - Magnetics, IEEE Transactions on

The effect of Fe, Cu, Zr, and Ti substitution on magnetic properties of SmCo 1 : 7 magnets at temperatures up to 500 C were studied. As-milled amorphous Sm(Co,Fe,Cu,Ti–Zr)7 magnets crystallized in the TbCu7-type structure after annealing at 750 C for 2 h. A room-temperature intrinsic coercivity of around 2.5 T is obtained for compositions SmCo6 4Zr0 2Ti0 4 and SmCo6 4Fe0 1Zr0 1Ti0 4. The high c...

متن کامل

RAPID COMMUNICATION Nanocomposite (Nd,Dy)(Fe,Co,Nb,B)5.5/α-Fe multilayer magnets with high performance

The structural and magnetic properties of rare-earth nanocomposite magnets of a (Nd,Dy)(Fe,Co,Nb,B)5.5 single layer and a (Nd,Dy)(Fe,Co,Nb,B)5.5/α-Fe multilayer prepared by sputtering and heat treatment have been investigated. Incomplete exchange coupling behaviour is observed in the Ti-buffered NdDyFeCoNbB + 40 wt%Fe single layer magnet. After annealing, the laminated nanostructure consisting ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2013