Preparation of Nano Particle Mg 0 . 2 Fe 0 . 8 O by Solution Combustion Method and Their Characterization
نویسنده
چکیده
The present paper investigated a preparation of Nano sized Mg0.2Fe0.8O by eco-friendly chemical combustion synthesis using magnesium and iron nitrates as oxidizers and the glycine as a fuel to drive the reaction. Powder characterization was carried out by X-ray diffraction (XRD) to estimate crystallite size, Particle Size Analyzer (PSA), Thermal gravimetric analyzer (TGA) for determining sample purity, weight loss percentage and decomposition reaction, Transmission electron microscope and Scanning electron microscope( SEM, TEM) were done to evaluation the morphology and average particle size. In this study are useful for establishing a simple method for the preparation of Mg0.2Fe0.8O Nano powders.
منابع مشابه
Preparation and characterization of nano-crystalline LiNi0.5Co0.5VO4 by tartate precursor combustion method
LiNi0.5Co0.5VO4 has been successfully synthesized by tartate precursor combustion method using Li2CO3, Co(NO3)2.6H2O, Ni(NO3)2.6H2O and NH4VO3 as a starting materials in deionized water with the subsequent calcination at 450-600 oC for 12 h. The combustion and decomposition of tartate precursor were studied by TGA and compared with tartaric acid. It found weight loss at 50-450 oC. The product s...
متن کاملPreparation and characterization of nano-crystalline LiNi0.5Co0.5VO4 by tartate precursor combustion method
LiNi0.5Co0.5VO4 has been successfully synthesized by tartate precursor combustion method using Li2CO3, Co(NO3)2.6H2O, Ni(NO3)2.6H2O and NH4VO3 as a starting materials in deionized water with the subsequent calcination at 450-600 oC for 12 h. The combustion and decomposition of tartate precursor were studied by TGA and compared with tartaric acid. It found weight loss at 50-450 oC. The product s...
متن کاملOne Step Rapid Synthesis of Nano-Crystalline ZnO by Microwave-Assisted Solution Combustion Method
In this study nano-crystalline ZnO particles were synthesized by microwave-assisted solution combustion method. Zinc nitrate and urea were used as oxidizer and fuel, respectively. The effect of fuel to oxidizer (F/O) ratio on ZnO powder properties was investigated by using different urea/nitrate ratios. X-ray diffractometer, scanning electron microscopy and fourier transform infra-red were used...
متن کاملSolution Combustion Preparation Of Nano-Al2O3: Synthesis and Characterization
The aluminum oxide materials are widely used in ceramics, refractories and abrasives due to their hardness, chemical inertness, high melting point, non-volatility and resistance to oxidation and corrosion. The paper describes work done on synthesis of α-alumina by using the simple, non-expensive solution combustion method using glycine as fuel.Aluminum oxide (Al2O3) nanoparticles were synthesiz...
متن کاملPreparation of Fe Substituted ZnO Nanoparticles and Investigation of Their Magnetic Behaviors
Nano-powders of diluted magnetic semiconductor Zn1-xFexO (0.0≤ x ≤0.1) were prepared via the sol-gel auto-combustion method. Crystal structure and phase identification carried out by X-Ray Diffraction (XRD) analysis. Mean crystallite size of the powders was estimated by Scherrer's formula. As M-H loops of the Fe substituted ZnO showed ferromagnetic behavior. The result...
متن کامل