Monodisperse face-centred tetragonal FePt nanoparticles with giant coercivity
نویسندگان
چکیده
Monodisperse face-centred tetragonal (fct) FePt nanoparticles with high magnetic anisotropy and, therefore, high coercivity have been prepared via a new heat treatment route. The as-synthesized face-centred cubic FePt nanoparticles were mixed with salt powders and annealed at 700 ̊C. The salts were then removed from the particles by washing the samples in water. Monodisperse fct FePt particles were recovered with the particle size and shape being retained. Coercivity of the isolated particles up to 30 kOe at room temperature has been obtained. (Some figures in this article are in colour only in the electronic version)
منابع مشابه
Magnetic hardening in ultrafine FePt nanoparticle assembled films
Ultrafine FePt nanoparticles have been synthesized via a novel chemical solution synthesis route. Without using a reducing agent, the stoichiometric FePt nanoparticles were produced by the decomposition of iron acetylacetonate and platinum acetylacetonate in octyl ether in the presence of oleic acid and oleyl amine as the surfactants. The particle size was found to be around 2 nm with a narrow ...
متن کاملMonodisperse FePt nanoparticles and ferromagnetic FePt nanocrystal superlattices
Synthesis of monodisperse iron-platinum (FePt) nanoparticles by reduction of platinum acetylacetonate and decomposition of iron pentacarbonyl in the presence of oleic acid and oleyl amine stabilizers is reported. The FePt particle composition is readily controlled, and the size is tunable from 3- to 10-nanometer diameter with a standard deviation of less than 5%. These nanoparticles self-assemb...
متن کاملA Novel Approach to Synthesis of FePt Magnetic Nanoparticles
Chemical reduction of ferric acetylacetonate (Fe(acac)3) and platinum acetylacetonate (Pt(acac)2) using polyol as a reducing agent as well as an effective surfactant, has successfully yielded monodisperse FePt nanoparticles with a size of approximately 2 nm. When annealed samples were compared to FePt nanoparticles synthesized using oleic acid and oleylamine as the surfactants under identical c...
متن کاملSynthesis and Morphology of Face Centered Cubic (FCC) Fe-Pt Nanoparticles
FePt nanoparticles with thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles are prepared by chemical synthesis and a salt-matrix annealing technique. Structural and magnetic characterizations confirm the phase transition from the disordered face-centered cubic structure. In this paper, 3 nm FePt nanoparticles are first synthesized by superhydride re...
متن کاملSynthesis and Morphology of Face Centered Cubic (FCC) Fe-Pt Nanoparticles
FePt nanoparticles with thermally stable room-temperature ferromagnetism are investigated. The monodisperse nanoparticles are prepared by chemical synthesis and a salt-matrix annealing technique. Structural and magnetic characterizations confirm the phase transition from the disordered face-centered cubic structure. In this paper, 3 nm FePt nanoparticles are first synthesized by superhydride re...
متن کامل