Synthesis, characterisation and catalytic properties of vanadium substituted mesoporous aluminophosphates
نویسندگان
چکیده
Vanadium substituted mesoporous AlPO have been synthesised using structure-directing surfactant under hydrothermal synthesis conditions. The presence of V in the framework of AlPO has been established by ESR, XPS, UV–vis DRS and ICP-AES measurements. This system is capable of promoting the oxidation of toluene to aldehyde and benzoic acid when the oxidising agent is 70% tert-butyl hydroperoxide while with 30% H2O2 cresols are formed. The activity of V-AlPO has been compared with those obtained with other similar porous materials like V-MCM 48, V-MCM-41, V-Al-Beta and VS-1. # 2004 Elsevier B.V. All rights reserved.
منابع مشابه
Nano composite mixed-addenda vanadium substituted polyoxometalate-TiO2 as a green, reusable and efficient catalyst for rapid and efficient synthesis of symmetric disulfides under ultrasound irradiation
Mixed-addenda vanadium substituted polyoxometalate supported on anatase TiO2 crushed nano leaf was synthesized by an unusual reaction with titanium tetraisopropoxide at 100 ºC via sol–gel method under oil-bath condition. The materials characterized by XRD, TEM, IR and UV–vis techniques. In the present work, efficient oxidative of thiols with polyoxometalate-TiO2/hydrogen peroxide ...
متن کاملOrganosilane surfactant-directed synthesis of mesoporous aluminophosphates constructed with crystalline microporous frameworks.
A direct hydrothermal assembly process was developed to synthesize mesoporous aluminophosphates that are constructed with crystalline microporous frameworks, by the addition of organosilane surfactants into the conventional synthesis composition for crystalline microporous aluminophosphates.
متن کاملSynthesis and photocatalytic activity of nanosized modified mesocellulous silica foams (MCFs) with PW12 and vanadium oxide
A series of tungestophosphoric acid and vanadium oxide supported on Mesocellulous Silica Foams (MCFs) featuring a well-defined three-dimensional (3D) mesoporosity were studied with regard to their performance in the photocatalytic activity to degrade Oezine Y (OY). This nanosized mesoporous catalyst (PW12@V-MCF) was characterized by FTIR, XRD, BET and TEM. XRD shows that the structure of MCF re...
متن کاملSynthesis, characterization, and catalytic performance of highly dispersed vanadium grafted SBA-15 catalyst
Vanadium oxide grafted on mesoporous silica SBA-15 has been synthesized using a controlled grafting process. Its structure has been thoroughly investigated using different characterization techniques, including N2-physisorption, X-ray diffraction, transmission electron microscopy (TEM), Raman spectroscopy, H2 temperature-programmed reduction, X-ray absorption near-edge structure (XANES), and ex...
متن کاملSynthesis and photocatalytic activity of nanosized modified mesocellulous silica foams (MCFs) with PW12 and vanadium oxide
A series of tungestophosphoric acid and vanadium oxide supported on Mesocellulous Silica Foams (MCFs) featuring a well-defined three-dimensional (3D) mesoporosity were studied with regard to their performance in the photocatalytic activity to degrade Oezine Y (OY). This nanosized mesoporous catalyst (PW12@V-MCF) was characterized by FTIR, XRD, BET and TEM. XRD shows that the structure of MCF re...
متن کامل