A high yield, one-pot dialysis-based process for self-assembly of near infrared absorbing gold nanoparticles.

HYPOTHESIS A facile, dialysis-based synthesis of stable near infrared (nIR) absorbing plasmonic gold nanoparticles (λmax=650-1000 nm) will increase the yield of nIR particles and reduce the amount of gold colloid contaminant in the product mixture. EXPERIMENTS Chloroauric acid and sodium thiosulfate were reacted using a dialysis membrane as a reaction vessel. Product yield and composition was determined and compared to traditional synthesis methods. The product particle distribution, yield, and partitioning of gold between dispersed product and membrane-adsorbed gold were determined. FINDINGS The synthesis results in polydisperse particle suspensions comprised of 70% spheroid-like particles, 27% triangular plates, and 3% rod-like structures with a 3% batch-to-batch variation and a prominent nIR absorption band with λmax=650-1000 nm. The amount of small gold colloid (λmax=530 nm; d<10 nm) in the isolated product was reduced by 96% compared to traditional methods. Additionally, 91.1% of the gold starting material is retained in the solution-based nanoparticle mixture while 8.2% is found on the dialysis membrane. The synthesis results in a quality ratio (QR=Abs(nIR)/Abs(530)) of 1.7-2.4 (twice that of previous techniques) and 14.3 times greater OD∗ml yield of the nIR-absorbing nanoparticle fraction.