δ25 Crack opening displacement parameter in cohesive zone models: experiments and simulations in asphalt concrete
نویسنده
چکیده
منابع مشابه
Simulation of the Mode I fracture of concrete beam with cohesive models
Crack propagation modeling in quasi-brittle materials such as concrete is essential for improving the reliability and load-bearing capacity assessment. Crack propagation explains many failure characteristics of concrete structures using the fracture mechanics approach. This approach could better explain the softening behavior of concrete structures. A great effort has been made in developing nu...
متن کاملMode I fracture of adhesive joints using tailored cohesive zone models
Cohesive zone models are explored in order to study cleavage fracture in adhesive bonded joints. A mode I cohesive model is defined which correlates the tensile traction and the displacement jump (crack faces opening) along the fracture process zone. In order to determine the traction-separation relation, the main fracture parameters, namely the cohesive strength and the fracture energy, as wel...
متن کاملUsing numerical simulations to compare the fracture toughness values for concrete from the size-effect, two-parameter and fictitious crack models
The size-effect, two-parameter, and fictitious crack models were developed to predict crack growth in materials like concrete that experience tension softening. The three models must predict the same response for infinitely large structures. Therefore, this study evaluates the differences in response for smaller structures. The metric used to compare response is the fracture toughness value req...
متن کاملGlobal sensitivity analysis in the identification of cohesive models using full-field kinematic data
Failure of adhesive bonded structures often occurs concurrent with the formation of a non-negligible fracture process zone in front of a macroscopic crack. For this reason, the analysis of damage and fracture is effectively carried out using the cohesive zone model (CZM). The crucial aspect of the CZM approach is the precise determination of the traction-separation relation. Yet it is usually d...
متن کاملA Cohesive Zone Model for Crack Growth Simulation in AISI 304 Steel
Stable ductile crack growth in 3 mm thick AISI 304 stainless steel specimens has been investigated experimentally and numerically. Multi-linear Isotropic Hardening method coupled with the Von-Mises yield criterion was adopted for modeling elasto-plastic behavior of the material. Mode-I CT fracture specimens have been tested to generate experimental load-displacement-crack growth data during sta...