Optical and current transport properties of CuO/ZnO nanocoral p-n heterostructure hydrothermally synthesized at low temperature
نویسندگان
چکیده
منابع مشابه
Low temperature solution process-based defect-induced orange-red light emitting diode
We report low-temperature solution-processed p-CuO nanorods (NRs)/n-ZnO NRs heterojunction light emitting diode (LED), exploiting the native point defects of ZnO NRs. ZnO NRs were synthesized at 90 °C by using hydrothermal method while CuO NRs were synthesized at 100 °C by using microwave reaction system. The electrical properties of newly synthesized CuO NRs revealed a promising p-type nature ...
متن کاملStudy of structural, optical and electrical properties of ZnO/CuO nanocomposites
In this work, the first ZnO/CuO nanocomposites were synthesized by chemical vapour deposition (CVD), thermal evaporation (PVD) and sputtering on silicon substrates (Si). Then, the structural, optical and electrical properties of the samples were investigated. Examination of the X-ray diffraction patterns confirmed the mixed-phase formation of hexagonal zinc oxide (ZnO) and monoclinic copper oxi...
متن کاملCuO/ZnO core/shell heterostructure nanowire arrays: synthesis, optical property, and energy application.
Aligned CuO nanowires (NWs) were synthesized by a simple cost-effective oxidation method. They act as cores; high density CuO/ZnO core/shell heterostructure NWs were fabricated by thermal decomposition. Using the core/shell heterostructure NWs as a photoelectrode, a 0.71% photo-to-hydrogen conversion efficiency was obtained from photoelectrochemical water decomposition.
متن کاملInvestigating structural, optical and photocatalytic properties of hydrothermally synthesized ZnO nanorod arrays with various aspect ratios
ZnO nanorods with various aspect ratios (by changing the time of growth between 0-240 min) were synthesized using hydrothermal method and were investigated using XRD, SEM, UV–Vis and PL. It was found that growth time is directly coupled with the length, orientation and aspect ratio of the nanorod arrays. The optical transmittance of the NR arrays indicated a regular decrement of average transmi...
متن کاملStudy on room temperature gas-sensing performance of CuO film-decorated ordered porous ZnO composite by In2O3 sensitization
For the first time, ordered mesoporous ZnO nanoparticles have been synthesized by a template method. The electroplating after chemical plating method was creatively used to form copper film on the surface of the prepared ZnO, and then a CuO film-decorated ordered porous ZnO composite (CuO/ZnO) was obtained by a high-temperature oxidation method. In2O3 was loaded into the prepared CuO film-ZnO b...