Acetalization of Carbonyl Compounds by Using Al2 (HPO4)3 under Green Condition Mg HPO4
نویسنده
چکیده
Al2(HPO4)3 was easily prepared and used as a solid acid in acetalization of carbonyl compounds at room temperature and under solvent-free conditions. The protection was done in short reaction times and in good to high isolated yields. The cheapness and availability of this reagent with easy procedure and work-up make this method attractive for the organic synthesis. Keywords—Acetalization, acid catalysis, carbonylcompounds, green condition, protection.
منابع مشابه
Transformations of the low-dimensional zinc phosphates to complex open-framework structures. Part 2:{ one-dimensional ladder to two- and three-dimensional structures
Open-framework zinc phosphates with one-dimensional ladder structures are shown to transform, under simple reaction conditions, to twoand three-dimensional structures. Thus, the one-dimensional ladder, [C6N4H22]0.5[Zn(HPO4)2], I, on heating with piperazine in aqueous solution gives a layer phosphate, [C4N2H12][Zn2(PO4)2], III, and the three-dimensional phosphates [C2N2H10]0.5[Zn(PO4)], IV, [C6N...
متن کاملIonothermal synthesis of open-framework metal phosphates with a Kagomé lattice network exhibiting canted anti-ferromagnetism† †Electronic supplementary information (ESI) available: Cif files, atomic parameters, X-ray diffraction patterns, IR spectra, TG curves, and thermal ellipsoid plot and atomic label schemes of compound 1–4. See DOI: 10.1039/c4tc00290c Click here for additional data file.
Four open-framework transition-metal phosphates; (NH4)2Co3(HPO4)2F4 (1), (NH4)Co3(HPO4)2(H2PO4)F2 (2), KCo3(HPO4)2(H2PO4)F2 (3), and KFe3(HPO4)2(H2PO4)F2 (4); are prepared by ionothermal synthesis using pyridinium hexafluorophosphate as the ionic liquid. Single-crystal X-ray diffraction analyses reveal that the four compounds contain cobalt/iron-oxygen/fluoride layers with Kagomé topology compo...
متن کاملTransformations of low-dimensional zinc phosphates to complex open-framework structures. Part 1: zero-dimensional to one-, two- and three-dimensional structures
Zero-dimensional 4-membered zinc phosphate monomers, [C6N2H18][Zn(HPO4)(H2PO4)2], I, and [C6N4H21][Zn(HPO4)2(H2PO4)], II, transform under simple reaction conditions to one-, twoand threedimensional structures. Monomer II, on heating with zinc acetate dihydrate (Zn(OAc)2) in aqueous solution, gives a layered phosphate [C6N4H21][NH4][Zn6(PO4)4(HPO4)2]H2O, III. A novel three-dimensional structure ...
متن کاملSynthesis of a novel organic-inorganic hybrid of polyaniline/titanium phosphate for Re(VII) removal.
The organic-inorganic hybrid material of polyaniline/titanium(IV) (PANI/Ti(HPO4)2) was synthesized by an oxidative polymerization reaction. The PANI/Ti(HPO4)2 was applied to remove Re(VII). The size of Ti(HPO4)2 nanoplates has no obvious effect on the sorption capacity. The effects of various environmental factors (such as pH, extra anions (NO3(-) and MO4(2-)) and temperature) on Re(VII) sorpti...
متن کاملMagnetic property studies of manganese-phosphate complexes.
Phosphoric acid forms two distinct coordination compounds with manganese salts in aqueous media, a two-dimensional layered structure, [Mn(HPO4).(H2O)3], 1, under ambient conditions, and a three-dimensional synthetic mineral, [Mn5(mu-OH2)2(HPO4)2(PO4)2(H2O)2], 2, under hydrothermal procedures, at 120 degrees C. In compound 1, the oxygen atom of the doubly deprotonated phosphoric acid interconnec...
متن کامل