Enhancing the superconducting temperature of MgB2 by SWCNT dilution

We report, for the first time, an increase in the superconducting critical temperature, TC of commercial ‘‘dirty’’ MgB2 by a nonsubstitutional hole-doping of the MgB2 structure using minute, single-wall carbon nanotube (SWCNT) inclusions. We varied the SWCNTs concentration from 0.05 wt% to 5 wt% and investigated the temperature-dependent resistivity from 10 K to 300 K. We used micro-Raman spectroscopy, field-emission scanning electron microscopy, and X-ray diffraction to analyze the interfacial interactions between the SWCNTs and the MgB2 grains. We obtained an increase in TC from 33.0 to 37.8 K (DTC 1⁄4 4:8 K), which is attributed to charge transfer from the MgB2 structure to the SWCNT structure. The charge transfer phenomenon is confirmed by micro-Raman analysis of the phonon states of the SWCNT tangential band frequency in the composites. We determined the charge transfer per carbon atom to be 0.0023/C, 0.0018/C and 0.0008/C for 0.05 wt%, 0.5 wt% and 5 wt% SWCNT inclusions, respectively, taking into account the contributions from the softening of the lattice constant and the nonadiabatic (dynamic) effects at the Fermi level. This report provides an experimental, alternative pathway to hole-doping of MgB2 without appealing to chemical substitution. 2013 Elsevier B.V. All rights reserved.