Lattice Misfit between Inclusion and Acicular Ferrite in Weld Metal of Low Carbon Low Alloy Steel

To clarify the mechanism of acicular ferrite formation in low carbon submerged arc weld metals of a Ti-B system with different aluminum contents, the lattice misfit between inclusion and acicular ferrite was investigated. The inclusions were directly sliced into thin foils by a focused ion beam device and crystallographic analyses were performed using a transmission electron microscope. These inclusions were surrounded by a narrow Ti-enriched layer which was identified as TiO. Our results showed that the Baker-Nutting orientation relationship was satisfied between the narrow TiO on the inclusion surface and acicular ferrite.