• Introduction • Steel Composition and Mechanical Properties • Welding of Steel • Microstructure of NUCu-OSM Steel • Estimate of Atmospheric Corrosion Resistance of NUCu-OSM Steel • Summary • Acknowledgment • References • Appendix 1. Monotonic Tensile Stress-Strain Curves for NUCu-OSM Steel • Appendix 2. Steel Compositions and Concentration Ranges in Data Bases Used for Atmospheric Corrosion Rate Estimates • Appendix 3. Corrosion Indices and Equations • Miscellaneous: subject index terms and author contact information
منابع مشابه
Copper Precipitation Hardened, High Strength, Weldable Steel
Steel containing 0.03% carbon, 1.35% copper and 0.84% nickel had yield strength in the 540-625 MPa (78-90 Ksi) range depending on thickness, ultimate tensile strength in the 625-690 MPa (90100 Ksi) range, and 25-30% elongation when air cooled after hot rolling. No brittle heat-affected zone was formed during manual or automatic submerged arc welding without pre-heating or postheating. The fract...
متن کاملInfluence of Cu and Ni on the Microstructure and Mechanical Properties of an HSLA Steel
In this research the role of alloying elements on the microstructure and mechanical properties of an as cast and hot rolled high strength low alloy (HSLA) steel was studied. Different compositions with different amount of copper in the presence of nickel, hot rolled and quenched in oil. Tensile test, hardness test, scanning electron microscope (SEM) and optical microscope (OM) were used to eval...
متن کاملComputer-aided design of transformation toughened blast resistant naval hull steels: Part I
A systematic approach to computer-aidedmaterials design has formulated a new class of ultratough, weldable secondary hardened plate steels combining new levels of strength and toughness while meeting processability requirements. A theoretical design concept integrated the mechanism of precipitated nickel-stabilized dispersed austenite for transformation toughening in an alloy strengthened by co...
متن کاملUnderstanding dual precipitation strengthening in ultra-high strength low carbon steel containing nano-sized copper precipitates and carbides
Low carbon ferritic steel alloyed with Ti, Mo and Cu was hot rolled and interrupt cooled to produce nano-sized precipitates of copper and (Ti,Mo)C carbides. The steel had a tensile strength of 840 MPa, an increase in yield strength of 380 MPa over that of the plain carbon steel and reasonable ductility. Transmission electron microscopy and small angle neutron scattering were used to characteriz...
متن کاملThe Effects of Hot Tear Segregations on the Rolled Product Quality of Continuously Cast Steel
The main objective of this project was to investigate the behavior and the damaging effects of hot tear segregations in the continuously cast steel blooms on the final product quality. To achieve this aim, plant data from three different types of steels were used. Investigations using the scanning electron microscope (SEM) equipped with energy dispersive x-ray spectroscopy (EDS) probe and metal...
متن کامل