The ZrO2 Formation in ZrB2/SiC Composite Irradiated by Laser
نویسندگان
چکیده
In order to clearly understand the details of ZrO₂ formation during ablation, high intensity continuous laser was chosen to irradiate ZrB₂/SiC. The results reveal that there are two different modes of ZrO₂ formation depending on whether liquid SiO₂ is present. When liquid SiO₂ is present, ZrO₂ generated by the oxidation of ZrB₂ is firstly dissolved into SiO₂. Then, ZrO₂ will precipitate again, the temperature will decrease and the SiO₂ will evaporate. Otherwise, the ZrB₂ will be oxidized to ZrO₂ directly.
منابع مشابه
سنتز و بررسی خواص نانو پودرکامپوزیتی ZrC-ZrB2-SiC
In this research, ZrC-ZrB2-SiC nanocomposite powder was synthesized by carbothermal and borocarbotermal reduction methods. Zirconium silicate was first milled for four hours Then eight mixtures of raw materials were prepared. Finally, the samples were pyrolyzed at 800 ° C for two hours and then heat-treated at 1500 ° C for 30 minutes under an argon atmosphere. X-ray diffraction (XRD) and scanni...
متن کاملEffect of Silicon Carbide and graphite additives on the pressureless Sintering mechanism and microstructural characteristics of Ultra-High Temperature ZrB2 Ceramics Composites
The effect of SiC content, additives, and process parameters on densification and microstructural properties of pressureless sintered ZrB2– (1–10 wt %) SiC particulate composites have been studied. The ZrB2–SiC composite powders mixed by Spex mixer with 1-2wt% C (added as graphite powder) and CMC have been cold-compacted and sintered in argon environment in the temperature range of 1800–2100ºC ...
متن کاملFabrication and inspection of C/Cf-ZrB2-ZrC-SiC and C/Cf-ZrB2-SiC composite parts resistant to ablation by pressureless sintering method
In this research, the aim is to achieve strong and ablation-resistant composite parts C / Cf-ZrB2-ZrC-SiC and C / Cf-ZrB2-SiC by non-pressure sintering method. C / Cf-ZrB2-SiC samples were prepared using synthesized ZrB2 and SiC powders between layers of resin-impregnated carbon fabric. After pressing with pressure 5 times at 1600 وC and heat treatment for 2 hours in a controlled atmosphere fur...
متن کاملPhase and Microstructural Correlation of Spark Plasma Sintered HfB2-ZrB2 Based Ultra-High Temperature Ceramic Composites
Abstract: The refractory diborides (HfB2 and ZrB2) are considered as promising ultra-high temperature ceramic (UHTCs) where low damage tolerance limits their application for the thermal protection system in re-entry vehicles. In this regard, SiC and CNT have been synergistically added as the sintering aids and toughening agents in the spark plasma sintered (SPS) HfB2-ZrB2 system. Herein, a nove...
متن کاملSynthesis of Al2O3-ZrO2 Nanocomposite by Mechanical Activated Self-propagating High Temperature Synthesis(MASHS) and Ignited via Laser
By consideration of unique properties of composite Al2O3-ZrO2 such as high toughness, high wear resistant and relative low thermal expansion, in this study, nanocomposite of Al2O3-ZrO2 was produced by Mechanical activated Self propagating High-temperature Synthesis (MASHS) using laser beam for ignition. First Al and ZrO2 powders were mixed in the mole ratio of 1:1 and milled for 1, 3 and 6 hour...