Bond strength of three luting agents to zirconia ceramic - Influence of surface treatment and thermocycling
نویسنده
چکیده
OBJECTIVE This in vitro study aimed to evaluate the influence of different surface treatments, 3 luting agents and thermocycling on microtensile bond strength (µTBS) to zirconia ceramic. MATERIAL AND METHODS A total of 18 blocks (5x5x4 mm) were fabricated from zirconia ceramic (ICE Zirkonia) and duplicated into composite blocks (Alphadent). Ceramic blocks were divided into 3 groups (n=6) according to the following surface treatments: airborne-particle abrasion (AA), silica-coating, (SC) (CoJet) and silica coating followed by silane application (SCSI) (ESPE Sil). Each group was divided into 3 subgroups (n=2) according to the 3 luting agents used. Resin-modified glass-ionomer cement (RMGIC, Ketac Cem Plus), self-adhesive resin cement (UN, RelyX Unicem) and adhesive resin cement (ML, MultiLink Automix) were used for bonding composite and zirconia blocks. Each bonding assembly was cut into microbars (10 mm long and 1±0.1 mm²). Seven specimens of each subgroup were stored in water bath at 37ºC for 1 week. The other 7 specimens were stored in water bath at 37ºC for 30 days then thermocycled (TC) for 7,500 cycles. µTBS values were recorded for each specimen using a universal testing machine. Statistical analyses were performed using a 3-way ANOVA model followed by serial 1-way ANOVAs. Comparison of means was performed with Tukey's HSD test at (α=0.05). RESULTS µTBS ranged from 16.8 to 31.8 MPa after 1 week and from 7.3 to 16.4 MPa after 30 days of storage in water and thermocycling. Artificial aging significantly decreased µTBS (p<0.05). Considering surface treatment, SCSI significantly increased µTBS (p<0.05) compared to SC and AA. Resin cements (UN and ML) demonstrated significantly higher µTBS (p<0.05) compared to RMGIC cement. CONCLUSIONS Silica coating followed by silane application together with adhesive resin cements significantly increased µTBS, while thermocycling significantly decreased µTBS.
منابع مشابه
Influence of nano-structured alumina coating on shear bond strength between Y-TZP ceramic and various dual-cured resin cements
PURPOSE The purpose of this study was to evaluate the effect of nano-structured alumina surface coating on shear bond strength between Y-TZP ceramic and various dual-cured resin cements. MATERIALS AND METHODS A total of 90 disk-shaped zirconia specimens (HASS CO., Gangneung, Korea) were divided into three groups by surface treatment method: (1) airborne particle abrasion, (2) tribochemicalsil...
متن کاملBond strength of three luting agents to zirconia thermocycling
O This in vitro treatments, 3 luting agents and thermocycling on microtensile bond strength (μTBS) to zirconia ceramic. Material and Methods: A total of 18 blocks (5x5x4 mm) were fabricated from zirconia ceramic (ICE Zirkonia) and duplicated into composite blocks (Alphadent). Ceramic blocks were divided into 3 groups (n=6) according to the following surface treatments: airborne-particle abrasio...
متن کاملمقایسه استحکام باند ریزبرشی سرامیکهای Cercon و Zirkonzahn با دو نوع سمان رزینی
Background and Aims: Nowadays, the application of all ceramic restorations are being raised, because of their physical characteristics, such as translucency and good appearance. Numerous researchers investigated the impact of surface treatments on the bond strength of zirconia ceramic with resin cements. The aim of this study was to compare the microshear bond strength of Cercon and Zirkonzah...
متن کاملBonding of Composite Resin to Alumina and Zirconia Ceramics with Special Emphasis on Surface Conditioning and Use of Coupling Agents
Timo Heikkinen. Bonding of Composite Resin to Alumina and Zirconia Ceramics with Special Emphasis on Surface Conditioning and Use of Coupling Agents. Department of Biomaterials Science, Institute of Dentistry, University of Turku. Annales Universitatis Turkuensis, Turku, Finland 2011. Dental oxide ceramics have been inspired by their biocompability and mechanical properties which have made dura...
متن کاملInfluence of storage conditions and effect of metal priming agents on bond strength of resin-modified glass ionomers to gold alloy.
This study evaluated the influence of water storage conditions and the effect of metal priming agents on bond strength and durability of four luting agents joined to gold alloy. Disk specimens were cast from a gold alloy (Degudent U), and the surfaces were ground flat with abrasive paper. Three surface conditions employed were: unprimed, primed with Alloy Primer, and primed with Metaltite. Thre...
متن کامل