Compression and impact testing of two-layer composite pyramidal-core sandwich panels
نویسندگان
چکیده
Quasi-static uniform compression tests and low-velocity concentrated impact tests were conducted to reveal the failure mechanisms and energy absorption capacity of two-layer carbon fiber composite sandwich panels with pyramidal truss cores. Three different volume-fraction cores (i.e., with different relative densities) were fabricated: 1.25%, 1.81%, and 2.27%. Two-layer sandwich panels with identical volumefraction cores (either 1.25% or 2.27%), and also stepwise graded panels consisting of one light and one heavy core, were investigated under uniform quasi-static compression. Under quasi-static compression, load peaks were identified with complete failure of individual truss layers due to strut buckling or strut crushing, and specific energy absorption was estimated for different core configurations. In the impact test, the damage resulting from low-velocity concentrated impact was investigated. Our results show that compared with glass fiber woven textile truss cores, two-layer carbon fiber composite pyramidal truss cores have comparable specific energy absorptions, and thus could be used in the development of novel light-weight multifunctional structures. 2011 Elsevier Ltd. All rights reserved.
منابع مشابه
Designing a prefabricated sandwich composite roofing system Made up of resisting facings and light-weight concrete core with truss-shaped connectors
In this paper, a new roofing system is introduced, which is constructued using the precast composite sandwich panels. This roofing sandwich panels system consists of three kinds of precast concrete sandwich panels including capital panels, beam or between columns panels, and slab or middle panels. The panels are composed of three layers; A high strength reinforced concrete top layer. A thick la...
متن کاملThree-dimensional Composite Lattice Structures Fabricated by Electrical Discharge Machining
We present a novel method for fabricating carbon fiber composite sandwich panels with lattice core construction by means of electrical discharge machining (EDM). First, flattop corrugated carbon fiber composite cores were fabricated by a hot press molding method. Then, two composite face sheets were bonded to each corrugated core to create precursor sandwich panels. These panels were transforme...
متن کاملMechanical behavior and failure of composite pyramidal truss core sandwich columns
A series of analytical and experimental investigations is presented to study the response and failure of pyramidal truss core sandwich panels made of carbon fiber composite under axial compression. In the analytical part of the study, three failure modes: (i) Euler or core shear macro-buckling, (ii) face wrinkling, and (iii) face sheet crushing, were considered and theoretical relationships for...
متن کاملEdgewise Compression Behavior of Three-Dimensional Integrated Woven Sandwich Composite Panels
متن کامل
An Investigation on Low Velocity Impact Response of Multilayer Sandwich Composite Structures
The effects of adding an extra layer within a sandwich panel and two different core types in top and bottom cores on low velocity impact loadings are studied experimentally in this paper. The panel includes polymer composite laminated sheets for faces and the internal laminated sheet called extra layer sheet, and two types of crushable foams are selected as the core material. Low velocity impac...