Effect of Oxygen Content on Microstructure and Mechanical Properties of Biomedical Ti-29Nb-13Ta-4.6Zr Alloy under Solutionized and Aged ConditionsThis Paper was Originally Published in Japanese in J. Japan Inst. Metals 72 (2008) 960--964

نویسندگان

  • Masaaki Nakai
  • Mitsuo Niinomi
  • Toshikazu Akahori
  • Harumi Tsutsumi
  • Michiharu Ogawa
چکیده

The effect of oxygen content on the microstructure and mechanical properties of the Ti-29mass%Nb-13mass%Ta-4.6mass%Zr (TNTZ) alloy was investigated in this study. The microstructural observation of TNTZ alloys, containing 0.1–0.4mass% oxygen, subjected to solution treatment shows the presence of a single phase. With an increase in oxygen content, the hardness, tensile strength, and Young’s modulus of TNTZ alloy increase, but its elongation decreases. Further, the phase precipitates in TNTZ alloys subjected to aging treatment at 723K for 259.2 ks. The results of transmission electron microscopy and X-ray diffraction analysis indicate that the size and volume fraction of the phase increase with oxygen content. Corresponding to the changes in the microstructure, the mechanical properties of TNTZ alloy subjected to aging treatment at 723K change with oxygen content. The increase in oxygen content leads to enhancement of the age hardening of TNTZ alloy, thereby increasing both tensile strength and Young’s modulus of TNTZ alloy, but its elongation decreases due to the -phase precipitation. The mechanical properties of TNTZ alloy (Young’s modulus: around 60–100GPa, tensile strength: around 600–1400MPa, and elongation: around 5–25%) vary significantly depending on oxygen content and heat treatment. [doi:10.2320/matertrans.MA200904]

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Isotropic plasticity of β-type Ti-29Nb-13Ta-4.6Zr alloy single crystals for the development of single crystalline β-Ti implants

β-type Ti-29Nb-13Ta-4.6Zr alloy is a promising novel material for biomedical applications. We have proposed a 'single crystalline β-Ti implant' as new hard tissue replacements for suppressing the stress shielding by achieving a drastic reduction in the Young's modulus. To develop this, the orientation dependence of the plastic deformation behavior of the Ti-29Nb-13Ta-4.6Zr single crystal was fi...

متن کامل

Influence of Alloy Elements on the Osteoconductivity of Anodized Ti-29Nb-13Ta-4.6Zr Alloy

Anodizing is expected to be an effective method to improve the osteoconductivity of the Ti-29Nb-13Ta-4.6Zr (TNTZ) alloy because the bioactivity of anodized Ti is good. However, it is not known how the alloy elements influence the surface roughness, composition, hydrophilicity, and osteoconductivity of the anodized film on the Ti alloy. In this study, we investigated the effects of anodizing on ...

متن کامل

In vivo osteoconductivity of surface modified Ti-29Nb-13Ta-4.6Zr alloy with low dissolution of toxic trace elements

Simulated Body Fluid (SBF) has served as a useful standard to check the bioactivity of implant materials for years. However, it is not perfectly able to imitate human serum; sometimes disparities between the SBF test and animal test were confirmed. Therefore, to ensure the reliability of the results of the SBF test obtained from our previous study, an animal study was performed to check osteoco...

متن کامل

High Bone Bonding Ability and Affinity of New Low-rigidity β-type Ti-29Nb-13Ta-4.6Zr Alloy as a Dental Implant

Hiroshi Edamatsu1, Tadashi Kawai1, Keiko Matsui1, Masaaki Nakai2, Tetsu Takahashi1, Seishi Echigo1, Mitsuo Niinomi2 and Shinji Kamakura3* 1Division of Oral and Maxillofacial Surgery, Department of Oral Medicine and Surgery, Tohoku University Graduate School of Dentistry, 4-1 Seiryomachi, Aoba-ku, Sendai 980-8575, Japan 2Department of Biomaterials Science, Institute for Materials Research, Tohok...

متن کامل

EFFECT OF SHORT HEAT TREATMENT ROUTES ON THE TRIBOLOGICAL PROPERTIES OF TI-6AL-4V ALLOY

In this research, the effect of annealing and aging temperature as well as the effect of quenching media on the microstructure, hardness and dry sliding wear behavior of Ti-6Al-4V alloy has been studied. Cylindrical samples with the diameter of 10 mm and the height of 20mm were solutionized at 930˚C and 1060˚C for 600 seconds and then were quenched in the cold water and in the air. The samples ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2009