Preparation of yttrium metal by reduction of yttrium trifluoride with calcium
نویسندگان
چکیده
The preparation of yttrium metal by the reduction of yttrium trifluoride with calcium is described. Alternate methods employing the formation of a low melting Y-Zn or Y-Mg intermediate alloy are evaluated and data on chemical and microscopic purity of the resulting metal are presented.
منابع مشابه
Preparation of rare earth metals
The production of over 400 grams of pure gadolinium metal by reduction of the anhydrous chloride by calcium in tantalum vessels is described; yields were over 97%. The use of the same techniques in an attempt to prepare yttrium metal were partially successful.
متن کاملProduction of yttrium aluminum silicate microspheres by gelation of an aqueous solution containing yttrium and aluminum ions in silicone oil
Background: Radioactive yttrium glass microspheres are used for liver cancer treatment. These yttrium aluminum silicate microspheres are synthesized from yttrium, aluminum and silicone oxides by melting. There are two known processes used to transform irregular shaped glass particles into microspheres, these ‘spheroidization by flame’ and ‘spheroidization by gravitational fall...
متن کاملThe Role of Factors Influencing the Optical Properties of Yttrium Aluminum Garnet Ceramic Body
Yttrium Aluminum Garnet (Y3Al5O12) is a transparent ceramic with a wide range of applications such as high mechanical strength windows, high power laser sources and radiation detectors. The most important challenge in making these ceramics is the problem of low light transmittance, especially in the visible area in the range of 400 to 700 nm, which is greatly affected and reduced by various fac...
متن کاملCathodic Electrodeposition and Characterization of YAG Nanostructure: Effect Current Density on the Morphology
Abstract YAG (Yttrium Aluminum Garnet) was successfully prepared through cathodic electrodeposition process using applying different current densities to the mixture of YCl3 and AlCl3 dissolved in water/ethanol 1:1 solution. Hydroxide precursors were cathodically grown on the cathode surface (at different current densities) and then the obtained hydroxide powder was heat-treated at 1100 °...
متن کاملSynthesis of Iron Yttrium Garnet Nanoparticles by Reverse Microemulsion Method
Colloidal nanodispersion of Iron Yttrium Garnet has been preparedbymixing the two ternary mixture of Triton X-100 (surfactant), n-heptane and aqueous solution that differing only in the aqueous phase.Ethanolwas added as cosurfactant and mixed them by ultrasound bath. By mixing these twomicroemulsions, Iron Yttrium garnet (Y3 Fe5 O12) nanodispersionwas obtained. Solids were settled by centrifuge...
متن کامل