PHYSICAL AND MECHANICAL PROPERTIES OF PLYWOOD MANUFACTURED FROM TREATED RED-HEART BEECH (Fagus Orientalis L.) WOOD VENEERS
نویسندگان
چکیده
Effects of drying temperature and artificial UV irradiation on the pH of veneer surfaces, water absorption, thickness swelling, as well as shear strength of plywood manufactured from untreated and treated veneer sheets were evaluated. Rotary cut veneer sheets from beech (Fagus orientalis Lipsky) log were selected. The veneer sheets were dried at either 100C or 180C after peeling. Then the surfaces were exposed to artificial UV irradiation in an UV chamber for 1, 2, and 3 days representing a natural sun irradiation of 2, 4, and 6 months, respectively. Tests by UV microspectrophotometry showed that after high temperature drying and UV irradiation treatment, lignin condensation occurs. Also with increasing drying temperature and UV irradiation duration phenolic extractives are mainly concentrated in parenchyma cells and vessel lumens. HPLC analysis of the treated tissue showed distinct signals of catechin and 2,6-dimethoxybenzoquinon, which are two chromophoric compounds in discolored red hearted beech wood. Increasing drying temperature up to 180C improved water absorption, thickness swelling, and shear strength of plywood samples. Especially, when veneers were exposed to UV irradiation (6 months), increased water absorption and thickness swelling and decreased the shear strength of plywood samples were observed.
منابع مشابه
Effects of Veneer Drying at High Temperature and Chemical Treatments on Equilibrium Moisture Content of Plywood
Moisture content (MC) is one of the most important factors that can affect many physical and mechanical properties of wood and veneers. MC strongly affects the final strength and durability of joints, development of surface checks in the wood and dimensional stability of the bonded assembly. In this study, plywood panels made from Alnus glutinosa (Alder), Fagus orientalis (Beech) and Picea orie...
متن کاملPhysical and Mechanical Properties of Particleboard Laminated with Thermally Compressed Veneer
The aim of this study was to investigate the effects of thermally compressed veneer laminating on some of the physical and mechanical properties of particleboard. Oriental beech (Fagus orientalis Lipsky) veneers were compressed under various press conditions. Commercially produced particleboard samples were laminated with such compressed veneer sheets. The density, 2-h and 24-h water absorption...
متن کاملEffect of Nanoclay-treated Uf Resin on the Physical and Mechanical 2 Properties of Plywood Manufactured with Wood from Tropical Fast
متن کامل
Comparison of Conventional Varnishes with Nanolacke UV Varnish With Respect to Hardness and Adhesion Durability
The long-term durability of varnished wooden surfaces used in either indoors or outdoors environments depends on the resistance of varnish layers on these surfaces against potential physical, mechanical and chemical effects to which they may be exposed. In this study, "Nanolacke ultraviolet varnish", developed by a Turkish dying and varnish industry company and widely accepted as a 21(st) centu...
متن کاملEffect of Nanoclay-treated Uf Resin on the Physical and Mechanical Properties of Plywood Manufactured with Wood from Tropical Fast Growth Plantations
Physical and mechanical properties were evaluated on cross-laminated panels (plywood) fabricated with three plantation species (Cordia alliodora, Gmelina arborea and Vochysia ferruginea) from tropical climates in Costa Rica. The panels were glued with urea-formaldehyde resin modified with nanoclay at four concentrations (0,75; 1,00; 1,50 and 2,00 %) and unmodified resin. It was determined that ...
متن کامل