Ultrahigh electrical conductivity in solution-sheared polymeric transparent films.
نویسندگان
چکیده
UNLABELLED With consumer electronics transitioning toward flexible products, there is a growing need for high-performance, mechanically robust, and inexpensive transparent conductors (TCs) for optoelectronic device integration. Herein, we report the scalable fabrication of highly conductive poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) ( PEDOT PSS) thin films via solution shearing. Specific control over deposition conditions allows for tunable phase separation and preferential PEDOT backbone alignment, resulting in record-high electrical conductivities of 4,600 ± 100 S/cm while maintaining high optical transparency. High-performance solution-sheared TC PEDOT:PSS films were used as patterned electrodes in capacitive touch sensors and organic photovoltaics to demonstrate practical viability in optoelectronic applications.
منابع مشابه
Influence of N2- and Ar-ambient annealing on the physical properties of SnO2: Co transparent conducting films prepared by spray pyrolysis technique
In this contribution, the Co doped SnO2 transparent semi-conducting films are prepared by spray pyrolysis technique and the influence of N2-and Ar-ambient annealing on their structural, electrical and optical properties are studied. The SnO2:Co thin films were deposited on the glass substrate at substrate temperature of 480 ˚C using an aqueous-ethanol solution consisting of tin and cobalt chlor...
متن کاملConductive Polythiophene Nanoparticles Deposition on Transparent PET Substrates: Effect of Modification with Hybrid Organic-inorganic Coating (RESEARCH NOTE)
In this work, Poly(ethyleneterephthalate) (PET) substrate was treated using KOH solution and was modified using hybrid O-I coating containing PCL )polycaprolactone( as organic phase and TEOS )tetraethoxysilane( as inorganic phase. The coating was prepared through a sol-gel process and applied on the surface by dip coater. Then, electrically conducting polythiophene (PTh) nanoparticles were depo...
متن کاملBuilding up Graphene-Based Conductive Polymer Composite Thin Films Using Reduced Graphene Oxide Prepared by γ-Ray Irradiation
In this paper, reduced graphene oxide (RGO) was prepared by means of γ -ray irradiation of graphene oxide (GO) in a water/ethanol mix solution, and we investigated the influence of reaction parameters, including ethanol concentration, absorbed dose, and dose rate during the irradiation. Due to the good dispersibility of the RGO in the mix solution, we built up flexible and conductive composite ...
متن کاملبررسی اثر باز پخت بر روی خواص الکتریکی و نوری لایههای نازک شفاف رسانای ساخته شده از نانولولههای کربنی- نانو سیم نقره
Transparent and conductive thin films of multi-walled carbon nanotube/ Ag nanowires were fabricated using spin coating technique. In order to improve the electrical conductivity and the optical properties, the layers were annealed from room temperature to 350 °C for 30 minutes. The measurements revealed that annealing caused electrical conductivity of fabricated thin layes to be improved. The o...
متن کاملReduction of graphene oxide films on Al foil for hybrid transparent conductive film applications
We report the reduction of graphene oxide (G-O) films on Al foil using hydrogen as a reducing agent generated during the etching of Al foil in an aqueous solution of hydrochloric acid (HCl). Complete etching of the Al substrate results in simultaneous reduction and a free standing film composed of stacked and overlapped reduced graphene oxide (RG-O) platelets. Generation of hydrogen at the G-O/...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Proceedings of the National Academy of Sciences of the United States of America
دوره 112 46 شماره
صفحات -
تاریخ انتشار 2015