Tm3+ and Yb3+ in TmXO4 and Yb3+ in YbXO4 (X = P, V) from 169Tm and 170 Yb Mössbauer measurements
نویسنده
چکیده
2014 Mössbauer measurements are reported on 169Tm3+ in TmPO4 and on 170Yb3+ in TmXO4 and in YbXO4 (X = P, V). The measured hyperfine parameters are used to provide information concerning the electronic properties of the rare earth ions. A set of crystalline electric field (CEF) parameters is obtained for Tm3+ in TmPO4 and previously proposed CEF parameters for Tm3+ in TmVO4 are discussed. The measured ground state properties of Yb3+ diluted into the two TmXO4 can be generated by sets of CEF parameters close to those obtained for Tm3+ in the corresponding matrix. Spin-spin relaxation rates were measured in the paramagnetic YbXO4 and the origin of the rate in YbVO4 is discussed. Magnetic ordering is observed in YbVO4 below about 0.15 K and also in YbPO4 in a comparable temperature zone. J. Physique 44 (1983) 833-839 JUILLET 1983,
منابع مشابه
Preparation and Characterization of Downconversion Luminescent LaVO4: Tm3+ , Yb3+ and Tm3+ /Yb3+ Nanosheets
Tm3+ , Yb3+ and Tm3+ /Yb3+ doped LaVO4 nanostructures were synthe- sized for the first time by using the hydrothermal method with the aid of La(CH3CO2)3 as lanthanum source in presence of oleic acid as surfactant. The products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), photoluminescence (PL) spectroscopy and ...
متن کاملSynthesis and upconversion luminescence of YF3:Yb3+ Tm3+ and TiO2-coated YF3:Yb3+, Tm3+ microcrystals.
YF3:Yb3+, Tm3+ microcrystals were prepared by a microemulsion method. The microcrystals were coated with TiO2 by hydrolysis of titanium n-butoxide (TBOT). Transform electron microscopy and X-ray diffraction were used to characterize the core/shell materials. The results indicated that the low TBOT/YF3 molar ratio was favorable to preparing the uniform TiO2 coatings. The upconversion luminescenc...
متن کامل1.84 m emission of Tm3+ sensitized by Yb3+ ions in monoclinic KGd„WO4...2 single crystals
By exciting at 940 nm, we have characterized the 1.84 m near infrared emission of trivalent thulium ions in Yb3+, Tm3+:KGd WO4 2 single crystals as a function of the dopant concentration and temperature, from 10 K to room temperature. An overall H6 Stark splitting of 470 cm −1 for the Tm3+ ions in the Yb3+, Tm3+:KGd WO4 2 was obtained. We also studied the blue emission at 476 nm Tm3+ and the ne...
متن کاملLu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کاملLu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کامل