Micro-sized nano-porous Si/C anodes for lithium ion batteries

: [email protected] .ac.cn (W. Han). Abstract The unique micro-sized (2–10 mm) Si/C composites consisting of 20 nm carbon coated secondary Si were synthesized from the abundant and low cost Al–Si alloy ingot by acid etching, ball-milling and carbonization procedure. The nano-porous Si/C composites provide a capacity of 1182 mAh g 1 at a current density of 50 mAg , 952 mAh g 1 at 200 mAg , 815 mAh g 1 at 500 mAg , and maintain 86.8% of initial capacity after 300 cycles. Even at a much higher current density of 10 A/g, the porous Si/C anode can still provide capacities of 4200 mAh g . Its superior rate capability and cycling stability of micro-sized nano-porous Si/C anodes is because it takes advantage of both long cycle life of nano-Si and high volumetric/gravimetric capacity of micro-Si. The hierarchical porous micro-scale Si/C with the carbon coating can stabilize the SEI layer and the inside pore provides adequate space for Si expansion, relaxing the stress/strain. The hierarchical Si/C with exceptional electrochemical performance is prepared by a simple, low-cost and saleable synthesis method, making it very promising for a large-scale production of high-performance Si-based anode materials in high-energy lithium-ion batteries. & 2014 Elsevier Ltd. All rights reserved.