Tensile Bond Strengths of Two Adhesives on Irradiated and Nonirradiated Human Dentin
نویسندگان
چکیده
The aim of this study was to assess the effect of radiotherapy on bond efficiency of two different adhesive systems using tensile bond strength test. Twenty extracted teeth after radiotherapy and twenty nonirradiated extracted teeth were used. The irradiation was applied in vivo to a minimal dose of 50 Gy. The specimens of each group were randomly assigned to two subgroups to test two different adhesive systems. A three-step/etch-and-rinse adhesive system (Optibond FL) and a two-steps/self-etch adhesive system (Optibond XTR) were used. Composite buildups were performed with a nanohybrid composite (Herculite XTR). All specimens were submitted to thermocycling ageing (10000 cycles). The specimens were sectioned in 1 mm(2) sticks. Microtensile bond strength tests were measured. Nonparametric statistical analyses were performed due to nonnormality of data. Optibond XTR on irradiated and nonirradiated teeth did not show any significant differences. However, Optibond FL bond strength was more effective on nonirradiated teeth than on irradiated teeth. Within the limitations of an in vitro study, it can be concluded that radiotherapy had a significant detrimental effect on bond strength to human dentin. However, it seems that adhesive choice could be adapted to the substrata. According to the present study, the two-steps/self-etch (Optibond XTR) adhesive system tested could be more effective on irradiated dentin compared to three-steps/etch-and-rinse adhesive system (Optibond FL).
منابع مشابه
Bond strengths of three different dentin adhesive systems to sclerotic dentin.
The two-fold aims of this study were: (1) to evaluate the microtensile bond strengths of different adhesive systems to sclerotic and sound palatal dentin; and (2) to observe the respective resin-dentin interfaces. Thirty extracted human incisor teeth were divided into two groups. Group I comprised sclerotic defects in the palatal zone. Group II comprised sound palatal dentin surfaces as control...
متن کاملBonding of self-etch and total-etch adhesives to carious dentin.
Carious dentin is partially demineralized and contains mineral crystals in the tubules. This may permit the deeper etching of intertubular dentin but prevent resin tag formation during bonding. We hypothesize that resin adhesives will produce lower bond strengths to caries-infected and caries-affected dentin compared with normal dentin. We tested this by measuring the microtensile bond strength...
متن کاملEffect of salivary contamination on shear bond strength of three different dentin adhesive systems
Effect of salivary contamination on shear bond strength of three different dentin adhesive systems Dr. H. Kermanshah* - Dr. H. Haj miragha** - Dr. SH. Gatoeizadeh*** *- Assistant Professor of Operative Dentistry Dept. - Faculty of Dentistry – Tehran University / Medical Sciences. **- Assistant Professor of Fixed Prosthodontics Dept. & Dental Research Center - Faculty of Dentistry – Tehran Unive...
متن کاملTensile bond strength of single-step self-etch adhesives to Er:YAG laser-irradiated dentin.
OBJECTIVE The purpose of this study was to evaluate the influence of Er:YAG laser irradiation on the bond strength to dentine of three single-step adhesives (AQ Bond Plus, G-Bond, and Clearfil Tri-S Bond), and one two-step self-etch adhesive (Clearfil Megabond) as a control. BACKGROUND DATA The vast majority of the numerous reports on resin bonding to Er:YAG-lased dentine have concluded that ...
متن کاملBonding of self-etching and total-etch systems to Er:YAG laser-irradiated dentin. Tensile bond strength and scanning electron microscopy.
This study investigated the effect of Er:YAG laser on bonding to dentin and the interaction pattern of different adhesive systems with the lased substrate. Tensile bond strength of a self-etching [Clearfil SE Bond (CSEB)] and two total-etch [Single Bond (SB) and Gluma One Bond (GOB)] systems to lased and non-lased dentin was evaluated and the adhesive interface morphology was examined by SEM. D...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
دوره 2015 شماره
صفحات -
تاریخ انتشار 2015