Hollow spheres of MCM-41 aluminosilicate with pinholes.
نویسندگان
چکیده
Hollow spheres of MCM-41 mesoporous aluminosilicates, with two small holes on the shell, have been synthesized from a surfactant-aluminosilicate gel composite.
منابع مشابه
"Tubules-Within-a-Tubule" Hierarchical Order of Mesoporous Molecular Sieves in MCM-41
The recently discovered mesoporous aluminosilicate MCM-41 consists of hexagonal arrays of nanometer-sized cylindrical pores. It is shown that this material can be synthesized by cooperative condensation of silicate and cylindrical cationic micelles. Careful control of the surfactant-water content and the rate of condensation of silica at high alkalinity resulted in hollow tubules 0.3 to 3 micro...
متن کاملSynthesis of open chain analogue of 1,8-dioxooctahydroxanthene catalyzed by aluminosilicate MCM- 41
In this study, aluminosilicate MCM-41 has been found to be an efficient catalyst for reaction betweendifferent benzaldehyde derivatives and 5,5-dimethyl-1,3-cyclohexanedione to give open chain analogue of1,8-dioxo-octahydroxanthene in excellent yields. No evidence for the formation of cyclization products wasobserved. The catalyst can be used several times after recovery.
متن کاملCharacterization of the acid sites in MCM-41-type materials by spectroscopic and catalytic techniques
Temperature-programmed desorption of pyridine, FTIR and multinuclear NMR spectroscopy and catalytic test reaction have been applied to investigate acid sites in mesoporous materials with silicon/aluminum ratios of 266 and 20 and in an amorphous aluminosilicate with nSi/nAl=5.4. The results obtained by these methods indicate the presence of weak Brønsted acid sites in the aluminosilicate samples...
متن کاملAdsorption behavior studies of Cerium on modified Mesoporous Aluminosilicate
In this paper, the adsorption of cerium on modified Mesoporous aluminosilicate (with Si/Al mole ratio of 10) was studied. The effects of pH, contact time, initial concentration of cerium on adsorption of cerium were investigated. The adsorption capacity was high in the pH range of 4-8 and decreases with decreasing of the pH value. The Langmuir and Freundlich isotherms were applied to represent ...
متن کاملMesoporous materials with zeolite framework: remarkable effect of the hierarchical structure for retardation of catalyst deactivation.
Hierarchical MFI zeolite was synthesized following a synthesis route using organic-inorganic hybrid surfactants; the resultant zeolite with mesoporous/microporous hierarchical structure exhibited remarkably high resistance to deactivation in catalytic activity of various reactions such as isomerization of 1,2,4-trimethylbenzene, cumene cracking, and esterification of benzyl alcohol with hexanoi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 19 شماره
صفحات -
تاریخ انتشار 2001